Inline coated biaxially oriented polyethylene foil and method for the production thereof
A biaxially oriented polyethylene foil (BOPE) is disclosed having layers (A) to (D), wherein layers (B) to (D) contain biaxially oriented polyethylene and layer (A) contains polyurethane and nanoparticles and has a layer thickness of 25 to 300 nm, layer (B) includes polymers having functional groups which are capable of forming covalent bonds with polyurethane and are directly connected to layer (A), layer (C) has at least a layer thickness of 50% of the total thickness of the foil and layer (D) represents an outer layer of the foil, which contains antiblocking agents.
1. A method for producing a polyethylene foil comprising 4 layers (A) to (D) arranged in the order of (A) to (D), wherein layers (B) to (D) comprise biaxially oriented polyethylene and wherein
layer (A) comprises polyurethane and nanoparticles and has a layer thickness of 25 to 300 nm,
layer (B) comprises polymers having functional groups, which can form covalent bonds with polyurethane and is directly connected to layer (A),
layer (C) has at least a layer thickness of 50% of the total thickness of the foil, and
layer (D) represents an outer layer of the foil and comprises antiblocking agents, the method comprising the steps of:
providing a film which is monoaxially stretched in the longitudinal direction, comprises layers (B) to (D) which have a composition, and wherein layers (B) and (D) are outer layers of the film,
applying a layer of a liquid dispersion containing polyurethane and nanoparticles to layer (B),
drying the liquid dispersion to produce layer (A),
stretching the film in the transverse direction to produce a biaxially oriented foil.
2. The method of claim 1 , further comprising:
providing a film comprising layers (B) to (D), which have a composition, in which the layers (B) to (D) are not oriented and layers (B) and (D) are outer layers of the film,
applying a liquid dispersion containing polyurethane and nanoparticles to layer (B),
drying the liquid dispersion by means of heating to produce layer (A),
simultaneously stretching the film in the longitudinal direction and in the transverse direction to produce a biaxially oriented foil.
3. The method according to claim 1 , wherein before applying the liquid dispersion, the surface of layer (B) is subjected to a surface treatment.
4. The method according to claim 1 , wherein the liquid dispersion is applied to layer (B) via inline coating.
5. The method according to claim 1 , wherein a wet layer formed by the liquid dispersion on layer (B) has a mass of 3 to 20 g/m 2 .
6. The method according to claim 1 , wherein the liquid dispersion is an aqueous dispersion.
7. The method according to claim 1 , wherein the stretching ratio in the longitudinal direction is in the range of from 2 to 8.
8. The method according to claim 1 , wherein the stretching ratio in the transverse direction is in the range of from 4 to 10.
9. The method according to claim 1 , wherein before applying the liquid dispersion, the surface of layer (B) is subjected to a corona treatment.
10. The method according to claim 1 , wherein the liquid dispersion is applied to layer (B) via inline coating using the reverse gravure kiss coating method.
11. The method according to claim 1 , wherein a wet layer formed by the liquid dispersion on layer (B) has a mass of 6 to 10 g/m 2 .