Method of manufacturing electrode
A method of manufacturing an electrode includes a step of preparing a granulated material containing an electrode active material, a binder, and a solvent, a step of compressing the granulated material between a pair of rolls, to form an electrode composite layer, and a step of placing the electrode composite layer on an electrode current collector. At least one of the pair of rolls has a temperature of 40° C. or higher.
1 . A method of manufacturing an electrode operatively associated with an apparatus, the method comprising:
preparing a granulated material containing an electrode active material, a binder, and a solvent;
heating a first roll, a second roll, and a third roll of the apparatus to a temperature equal to or higher than 40° C.;
compressing the granulated material between the first roll and the second roll;
forming an electrode composite layer;
conveying an electrode current collector on the third roll; and
pressing the electrode composite layer, onto the electrode current collector conveyed on the third roll.
2 . The method according to claim 1 , wherein the granulated material has a solid content percentage that is equal to or greater than 75 mass % and equal to or less than 90 mass %.
3 . The method according to claim 1 , further comprising adjusting a rotational speed of the second roll faster than a rotational speed of the first roll during compressing the granulated material between the first roll and the second roll.
4 . The method according to claim 1 , further comprising pressing the electrode composite layer onto the electrode current collector conveyed on the third roll, by passing the electrode composite layer through a first gap between the second roll and the third roll.
5 . The method according to claim 4 , further comprising:
compressing the granulated material between the first roll and the second roll, by passing the granulated material containing through a second gap between the first roll and the second roll; and
preparing the first roll, the second roll, and the third roll such that the first gap is 20 μm, and the second gap is 50 μm.
6 . The method according to claim 1 , further comprising preparing the electrode active material having an average particle diameter of 1 to 25 μm.
7 . The method according to claim 1 , further comprising preparing the first roll, the second roll, and the third roll, each having a diameter of 10 to 1000 mm and an axial length of 100 to 2000 mm.
8 . The method according to claim 1 , further comprising heating the first roll, the second roll, and the third roll to a temperature equal to or lower than 100° C.
9 . The method according to claim 1 , further comprising mixing water and a polar organic solvent to prepare the solvent.
10 . The method according to claim 1 , further comprising preparing the electrode active material including lithium metal oxides.
11 . The method according to claim 1 , further comprising preparing the binder including carboxymethyl cellulose, styrene butadiene rubber, polyvinylidene fluoride, polytetrafluoroethylene, and polyacrylic acid.
12 . The method according to claim 1 , further comprising
preparing the electrode active material having an average particle diameter of 1 to 25 μm;
preparing the first roll, the second roll, and the third roll, each having a diameter of 10 to 1000 mm and an axial length of 100 to 2000 mm;
heating the first roll, the second roll, and the third roll to a temperature equal to or lower than 100° C.;
mixing water and a polar organic solvent to prepare the solvent;
preparing the electrode active material including lithium metal oxides;
preparing the binder including carboxymethyl cellulose, styrene butadiene rubber, polyvinylidene fluoride, polytetrafluoroethylene, and polyacrylic acid;
pressing the electrode composite layer onto the electrode current collector conveyed on the third roll, by passing the electrode composite layer through a first gap between the second roll and the third roll;
compressing the granulated material between the first roll and the second roll, by passing the granulated material containing through a second gap between the first roll and the second roll; and
preparing the first roll, the second roll, and the third roll such that the first gap is 20 μm, and the second gap is 50 μm.