Exemplary barrier additive compositions have useful barrier properties. An exemplary barrier additive composition includes a nylon 6, a compatibilizer including maleic anhydride grafted polyethylene or polypropylene, and an optional optical tracer. The barrier additive composition can be used in containers for liquid chemicals, such as petroleum derived products. Also disclosed are polymer blends and films that include the barrier additive composition, methods of making the barrier additive composition, and methods of making containers and films that include the barrier additive composition.
1. A barrier additive composition comprising:
no less than 55 weight % of a nylon 6;
a compatibilizer comprising maleic anhydride grafted polyethylene or polypropylene, wherein the maleic anhydride is grafted at greater than 0.5% to less than 1.5% by weight of the polyethylene or polypropylene; and
an ultraviolet tracer.
2. The barrier additive composition of claim 1 , wherein the nylon 6 has a number average molecular weight of greater than 2000 Daltons.
3. The barrier additive composition of claim 1 , wherein the nylon 6 has a specific gravity of about 1.06 g/cm 3 to about 1.14 g/cm 3 , a melting point of about 220° C. to about 235° C., a flexural modulus of about 250,000 psi to about 450,000 psi, or a combination thereof.
4. The barrier additive composition of claim 1 , wherein the barrier additive composition comprises the nylon 6 at about 55% to about 80% by weight of the composition.
5. The barrier additive composition of claim 1 , wherein the compatibilizer has a specific gravity of about 0.875 g/cm 3 to about 0.960 g/cm 3 , a melting point of about 63° C. to about 130° C., or a combination thereof.
6. The barrier additive composition of claim 1 , wherein the barrier additive composition comprises the compatibilizer at about 25% to less than 45% by weight of the composition.
7. The barrier additive composition of claim 1 , wherein the polyethylene of the compatibilizer is selected from the group consisting of a linear low-density polyethylene, a low-density polyethylene, a high density polyethylene, and a combination thereof.
8. The barrier additive composition of claim 1 , wherein the polyethylene of the compatibilizer has a density of about 0.92 g/cm 3 to about 0.97 g/cm 3 .
9. The barrier additive composition of claim 1 , wherein the maleic anhydride is grafted at about 1% to about 1.3% by weight of the polyethylene or polypropylene.
10. The barrier additive composition of claim 1 , wherein the barrier additive composition comprises the ultraviolet tracer at about 0.5% to about 5% by weight of the composition.
11. A method of making a barrier additive composition, the method comprising:
blending a nylon 6, a compatibilizer, and an ultraviolet tracer, the compatibilizer comprising maleic anhydride grafted polyethylene or polypropylene, wherein the maleic anhydride is grafted at greater than 0.5% to less than 1.5% by weight of the polyethylene or polypropylene, in a melt phase to form a barrier additive blend, the barrier additive blend comprising no less than 55 weight % of the nylon 6, and
extruding the barrier additive blend into pellets.
12. The method of claim 11 , wherein the nylon 6 is sprayed with the ultraviolet tracer before blending with the compatibilizer, the pellets are sprayed with the ultraviolet tracer, or a combination thereof.
13. A barrier additive composition consisting essentially of:
no less than 55 weight % of a nylon 6;
a compatibilizer comprising maleic anhydride grafted polyethylene or polypropylene, wherein the maleic anhydride is grafted at greater than 0.5% to less than 1.5% by weight of the polyethylene or polypropylene; and
an ultraviolet tracer.