Hot melt adhesive composition having improved wet bonding strength
The invention relates to a hot melt adhesive composition comprising a polymer component, the polymer component comprising at least one styrene-butadiene-styrene block copolymer P having a styrene content from 35 to 50% by weight: a styrene-butadiene diblock content from 50 to 80% by weight; and a viscosity of a 15% by weight toluene solution at 25° C. of 20 to 40 mPa·s, and at least one styrene block copolymer other than a styrene-butadiene-styrene block copolymer, wherein said styrene-butadiene-styrene block copolymer P is at a content from 10 to 40% by weight relative to the total weight of the polymer component. The invention also relates to the use of said composition as an adhesive for bonding two substrates, and to articles comprising at least one interior or exterior surface coated with said composition.
1. A hot melt adhesive composition comprising a polymer component, the polymer component comprising:
at least one linear styrene-butadiene-styrene block copolymer P having:
a styrene content from 35 to 50% by weight;
a styrene-butadiene diblock content from 50 to 80% by weight; and
a viscosity of a 15% by weight toluene solution at 25° C. of 20 to 40 mPa·s;
at least one styrene block copolymer other than a styrene-butadiene-styrene block copolymer, the styrene block copolymer comprising a styrene-isoprene-styrene block copolymer;
wherein said styrene-butadiene-styrene block copolymer P is at a content from 10 to 40% by weight relative to the total weight of the polymer component.
2. The composition according to claim 1 , wherein the styrene-butadiene-styrene block copolymer P is at a content from 10 to 35% by weight relative to the total weight of the polymer component.
3. The composition according to claim 1 , wherein the at least one styrene block copolymer other than a styrene-butadiene-styrene block copolymer is a mixture of styrene-isoprene-styrene copolymer and a styrene block copolymer selected from the group consisting of styrene-butadiene, styrene-isoprene, styrene-isoprene-butadiene-styrene, styrene-ethylene-butylene-styrene, styrene-ethylene-butylene, styrene-ethylene-propylene-styrene, styrene-ethylene propylene, styrene-ethylene-ethylene-propylene-styrene copolymers, and mixtures thereof.
4. The composition according to claim 1 , wherein the at least one styrene block copolymer other than a styrene-butadiene-styrene is a styrene-isoprene-styrene block copolymer.
5. The composition according to claim 1 , wherein the at least one styrene block copolymer other than a styrene-butadiene-styrene is at a content from 0.1 to 60% by weight relative to the total weight of the polymer component.
6. The composition according to claim 1 wherein the polymer component comprises:
from 40 to 85 wt. % of at least one styrene-butadiene-styrene block copolymer different from the styrene-butadiene-styrene block copolymer P;
from 1 to 20 wt. % of a styrene-isoprene-styrene block copolymer.
7. The composition according to claim 1 being devoid of a resin, wax or oil modified by an unsaturated polycarboxylic acid, anhydride or ester.
8. The composition according to claim 1 , having a viscosity from 1,000 to 30,000 mPa·s at a temperature of 120° C.
9. The composition according to claim 1 , wherein the total amount of polymer component is from 10% to 80% by weight relative to the total weight of the hot melt adhesive composition.
10. The composition according to claim 1 , further comprising from 45 to 75% of a tackifying resin relative to the total weight of the composition, and/or from 5 to 25% of a plasticizer relative to the total weight of the composition, and/or from 0.1 to 5% of a stabilizer relative to the total weight of the composition, and/or from 0 to 30% of a wax relative to the total weight of the composition.
11. An adhesive or a coating comprising the composition according to claim 1 , wherein the adhesive is used for bonding two substrates together, or the coating is used on the surface of a substrate.
12. An article comprising at least one interior or exterior surface coated with the hot melt adhesive composition of claim 1 .
13. The article of claim 12 , wherein the interior or exterior surface is a nonwoven fabric.
14. The article according to claim 12 , wherein the article is selected from the group consisting of a disposable diaper, disposable training pants, a feminine sanitary napkin, an adsorbent pad, a surgical mask, and a surgical coat.
15. The hot melt adhesive composition of claim 1 , wherein the at least one styrene-butadiene-styrene block copolymer P has:
a styrene content from 40 to 45% by weight; and
a styrene-butadiene diblock content from 60 to 70% by weight.
16. The hot melt adhesive composition of claim 1 , wherein the polymer component comprises:
from 40 to 85 wt. % of at least one styrene-butadiene-styrene block copolymer different from the styrene-butadiene-styrene block copolymer P; and
from 5 to 15 wt. % of a styrene-isoprene-styrene block copolymer.
17. The hot melt adhesive composition of claim 1 , wherein the at least one styrene block copolymer other than a styrene-butadiene-styrene block copolymer is a mixture of linear styrene-isoprene-styrene copolymer and styrene-isoprene copolymer.