Ceramic sintered body comprising magnesium aluminate spinel
Disclosed is a ceramic sintered body comprising magnesium aluminate spinel of composition MgAl 2 O 4 having from 90 to 100% by volume of a cubic crystallographic structure and a density of from 3.47 to 3.58 g/cc, wherein the ceramic sintered body is free of sintering aids. A method of making the ceramic sintered body comprising spinel is also disclosed.
1. A method of making a ceramic sintered body, the method comprising the steps of:
a. combining magnesium oxide powder and aluminum oxide powder to make a powder mixture, wherein the powder mixture has a total purity of higher than 99.995%;
b. calcining the powder mixture by applying heat to raise the temperature of the powder mixture to a temperature of from 600° C. to 1000° C. and maintaining the calcination temperature for a duration of from 4 to 12 hours to form a calcined powder mixture;
c. disposing the calcined powder mixture inside a volume defined by a tool set of a sintering apparatus and creating vacuum conditions inside the volume;
d. applying from 5 to 60 MPa of pressure to the calcined powder mixture while heating to a sintering temperature of from 1000 to 1700° C. and performing sintering to form the ceramic sintered body; and,
e. lowering the temperature of the ceramic sintered body, wherein the ceramic sintered body comprises magnesium aluminate spinel of composition MgAl 2 O 4 having from 90 to 100% by volume of a cubic crystallographic structure and a density of from 3.47 to 3.58 g/cc.
2. The method of claim 1 wherein the powder mixture is devoid of elemental lithium and lithium compounds.
3. The method of claim 1 wherein the tool set comprises a graphite die having a volume, an inner wall, a first and second openings, and first and second punches operatively coupled with the die, wherein each of the first and second punches have an outer wall defining a diameter that is less than a diameter of the inner wall of the die thereby creating a gap between each of the first and second punches and the inner wall of the die when at least one of the first and second punches moves within the volume of the die.
4. The method of claim 3 wherein the gap is a distance of from 10 to 100 um between the inner wall of the die and the outer wall of each of the first and second punches.
5. The method according to claim 1 wherein the sintering temperature is from 1000 to 1500° C.
6. The method according to claim 1 wherein from 5 to 59 MPa of pressure is applied to the calcined powder mixture while heating to the sintering temperature.
7. The method according to claim 1 wherein less than 50 MPa of pressure is applied to the calcined powder mixture while heating to the sintering temperature.
8. The method according to claim 1 wherein the sintered ceramic body has a greatest dimension of from 100 mm to 622 mm.
9. The method according to claim 8 wherein the sintered ceramic body has a greatest dimension of from 200 mm to 622 mm.
10. The method according to claim 1 wherein the ceramic sintered body has a density variance of from 0.2 to less than 5% as measured across the greatest dimension.
11. The method according to claim 1 wherein the calcined powder mixture comprises aluminum oxide and magnesium oxide.
12. The method according to claim 1 further comprising the steps of:
f. annealing the ceramic sintered body by applying heat to raise the temperature of the ceramic sintered body to reach an annealing temperature, performing annealing; and
g. lowering the temperature of the annealed ceramic sintered body.
13. The method according to claim 12 further comprising the step of:
h. machining the ceramic sintered body to create a ceramic sintered body component in the shape of a cube, a disk, a plate, a ring, a cylinder, a curved plate, a tube, a dome, a window, a ring, a nozzle, a chuck, a showerhead, an injector.
14. A ceramic sintered body for production of semiconductor manufacturing chamber components made by the process of claim 1 .