Lithographic photopolymer printing plate precursor with improved daylight stability
A lithographic printing plate precursor is disclosed which comprises a support, a photopolymerizable image recording layer and an overcoat which comprises a low-molecular radical inhibitor. After image-wise exposure, the plate is heated whereby the radical inhibitor diffuses from the overcoat to the image recording layer, resulting in an increase of the daylight stability of the exposed and heated precursor. Such plate is especially suitable for on-press processing.
1. A lithographic printing plate precursor comprising a support and provided thereon, in order,
a negative working image recording layer which undergoes a free-radical polymerization or crosslinking reaction upon exposure to ultraviolet, violet, or infrared light and
an overcoat which comprises (a) a low-molecular radical inhibitor, which is an organic compound having a molecular weight of less than 1000 Dalton, or (b) a polymer which releases a low-molecular radical inhibitor, which is an organic compound having a molecular weight of less than 1000 Dalton, upon heating, wherein the low-molecular radical inhibitor is present or released in the overcoat in an amount of at least 10 mg/m 2 ,
characterized in that upon heating said low-molecular radical inhibitor is capable of diffusing to the image recording layer, thereby rendering the image recording layer less sensitive to daylight than before said heating.
2. The printing plate precursor of claim 1 , wherein the image recording layer has a daylight stability after heating of at least 30000 lux·min.
3. The printing plate precursor of claim 1 , wherein the image recording layer has a daylight stability after heating of at least 60000 lux·min.
4. The printing plate precursor of claim 1 , wherein the low-molecular radical inhibitor is a nitroxyl compound.
5. The printing plate precursor of claim 2 , wherein the low-molecular radical inhibitor is a nitroxyl compound.
6. The printing plate precursor of claim 1 , wherein the image recording layer comprises one or more compounds having a chemical structure according to Formula:
wherein n represents an integer equal to 0 or 1, L 1 represents a divalent linking group, and * denotes a chemical bond to the rest of the structure.
7. The printing plate precursor of claim 2 , wherein the image recording layer comprises one or more compounds having a chemical structure according to Formula:
wherein n represents an integer equal to 0 or 1, L 1 represents a divalent linking group, and * denotes a chemical bond to the rest of the structure.
8. A method of making a lithographic printing plate comprising the steps of:
(a) image-wise exposing the lithographic printing plate precursor of claim 1 to ultraviolet, violet or infrared light;
(b) heating the plate precursor, thereby inducing diffusion of the low-molecular radical inhibitor to the image recording layer and rendering the image recording layer less sensitive to daylight than before said heating; and
(c) processing the plate precursor.
9. The method of claim 8 , wherein step (c) is carried out by mounting the plate precursor on a plate cylinder of a lithographic printing press and rotating the plate cylinder while feeding fountain solution and/or ink to the plate precursor.
10. The method of claim 9 , wherein during step (b) the plate precursor is heated for 1 to 10 minutes at a temperature from 120° C. to 200° C.
11. The method of claim 10 , wherein the image recording layer has a daylight stability after the heating step (b) of at least 30000 lux·min.
12. A method of making a lithographic printing plate comprising the steps of:
(a) image-wise exposing the lithographic printing plate precursor of claim 4 to ultraviolet, violet or infrared light;
(b) heating the plate precursor, thereby inducing diffusion of the low-molecular radical inhibitor to the image recording layer and rendering the image recording layer less sensitive to daylight than before said heating; and
(c) processing the plate precursor.
13. The method of claim 12 , wherein step (c) is carried out by mounting the plate precursor on a plate cylinder of a lithographic printing press and rotating the plate cylinder while feeding fountain solution and/or ink to the plate precursor.
14. The method of claim 13 , wherein during step (b) the plate precursor is heated for 1 to 10 minutes at a temperature from 120° C. to 200° C.
15. The method of claim 14 , wherein the image recording layer has a daylight stability after the heating step (b) of at least 30000 lux·min.
16. A method of making a lithographic printing plate comprising the steps of:
(a) image-wise exposing the lithographic printing plate precursor of claim 6 to ultraviolet, violet or infrared light;
(b) heating the plate precursor, thereby inducing diffusion of the low-molecular radical inhibitor to the image recording layer and rendering the image recording layer less sensitive to daylight than before said heating; and
(c) processing the plate precursor.
17. The method of claim 16 , wherein step (c) is carried out by mounting the plate precursor on a plate cylinder of a lithographic printing press and rotating the plate cylinder while feeding fountain solution and/or ink to the plate precursor.
18. The method of claim 17 , wherein during step (b) the plate precursor is heated for 1 to 10 minutes at a temperature from 120° C. to 200° C. and the image recording layer has a daylight stability after the heating step (b) of at least 30000 lux·min.