The present invention relates to carbon nanotubes which are characterized by satisfying the requirements (1) to (3) described below. (1) An aqueous dispersion liquid of the carbon nanotubes has a pH of from 8.0 to 10.0. (2) The BET specific surface area of the carbon nanotubes is from 200 to 800 m 2 /g. (3) IfY is the average fiber length (nm) of the carbon nanotubes and X is the BET specific surface area (m 2 /g) of the carbon nanotubes, X and Y satisfy Y = -aX + b (wherein a and b represent constants, while satisfying 2.2≤a≤3.5 and 2,300≤b≤5,000).
1 . Carbon nanotubes, that satisfy following (1) to (3):
(1) a pH of a carbon nanotube aqueous dispersion liquid is 8.0 to 10.0;
(2) a BET specific surface area of the carbon nanotubes is 200 m 2 /g to 800 m 2 /g; and
(3) Y=-aX+b (a and b are constants, 2.2≤a≤3.5, 2,300≤b≤5,000) when an average fiber length (nm) of the carbon nanotubes is Y, and the BET specific surface area (m 2 /g) of the carbon nanotubes is X.
2 . The carbon nanotubes according to claim 1 ,
wherein, in a Raman spectrum of the carbon nanotubes, a G/D ratio is 0.5 to 4.5 when a maximum peak intensity in a range of 1,560 cm -1 to 1,600 cm -1 is G, and a maximum peak intensity in a range of 1,310 cm -1 to 1,350 cm -1 is D.
3 . The carbon nanotubes according to claim 1 ,
wherein an average outer diameter of the carbon nanotubes is 5 nm to 20 nm.
4 . The carbon nanotubes according to claim 1 ,
wherein a volume resistivity of the carbon nanotubes is 1.0×10 -2 Ω·cm to 3.0×10 - 2 Ω·cm.
5 . A carbon nanotube dispersion liquid comprising the carbon nanotubes according to claim 1 , a dispersant, and an aqueous liquid medium.
6 . The carbon nanotube dispersion liquid according to claim 5 ,
wherein a complex modulus of elasticity of the carbon nanotube dispersion liquid is 1 Pa to 100 Pa.
7 . The carbon nanotube dispersion liquid according to claim 5 ,
wherein the product (X×Y) of a complex modulus of elasticity X (Pa) and a phase angle Y(°) of the carbon nanotube dispersion liquid is 100 or more and 1,500 or less.
8 . The carbon nanotube dispersion liquid according to claim 5 , which contains 10 parts by mass to 100 parts by mass of the dispersant with respect to 100 parts by mass of the carbon nanotubes.
9 . The carbon nanotube dispersion liquid according to claim 5 ,
wherein a pH is 7 to 11.
10 . The carbon nanotube dispersion liquid according to claim 5 ,
wherein a 50% particle size (D50) calculated according to laser diffraction particle size distribution measurement is 1 µm to 20 µm.
11 . The carbon nanotube dispersion liquid according to claim 5 , which is a dispersion liquid containing 0.4 parts by mass or more and 2.5 parts by mass or less of carbon nanotubes in 100 parts by mass of the carbon nanotube dispersion liquid, and in which, when a viscosity of the carbon nanotube dispersion liquid measured at 6 rpm using a B type viscometer is α, and the viscosity of the carbon nanotube dispersion liquid measured at 60 rpm is β, α/β satisfies 2.0≤α/β≤6.0.
12 . A carbon nanotube resin composition comprising the carbon nanotube dispersion liquid according to claim 5 , and a binder resin.
13 . The carbon nanotube resin composition according to claim 12 ,
wherein the binder resin includes at least one selected from the group consisting of carboxymethyl cellulose, styrene butadiene rubber, and polyacrylic acid.
14 . A mixture slurry comprising the carbon nanotube resin composition according to claim 12 , and an active material.
15 . An electrode film which is a coating film of the mixture slurry according to claim 14 .
16 . A nonaqueous electrolyte secondary battery, comprising a positive electrode, a negative electrode, and an electrolyte,
wherein at least one of the positive electrode and the negative electrode includes the electrode film according to claim 15 .
17 . A nonaqueous electrolyte secondary battery comprising the carbon nanotubes according to claim 1 .
18 . A vehicle comprising the nonaqueous electrolyte secondary battery according to claim 16 .