MAGNETIC RESIN COMPOSITION FOR INJECTION MOLDING, AND INJECTION MOLDED BODY FOR MAGNETIC SHIELDS
A magnetic resin composition uses, as magnetic particles (B), scale-like particles that are formed of an Fe—Si—Al alloy, and has a mass ratio of a thermoplastic resin (A) that has a melting point of from 100° C. to 400° C. to the Fe—Si—Al alloy of from 10/90 to 15/85; and a cross-sectional surface ( 52 ) in the thickness direction of a sheet ( 50 ) that is formed from this magnetic resin composition (1) satisfies the conditions (1) and (2) described below. (1) The total area of the magnetic particles (B) subjected to image processing is from 40% to 65% of the area of the image processing region. (2) The number of the magnetic particles (B) subjected to image processing is from 200 to 500.
1 . A magnetic resin composition for injection molding comprising a thermoplastic resin (A) that has a melting point of 100° C. to 400° C. and magnetic particles (B), wherein
as the magnetic particles (B), scale-like particles that are formed of an Fe—Si—Al alloy are used, and a mass ratio of the thermoplastic resin (A) to the Fe—Si—Al alloy, that is, thermoplastic resin (A)/Fe—Si—Al alloy is 10/90 to 15/85, and
conditions (1) and (2) described below are satisfied when, in order to form the magnetic resin composition for injection molding into a shape of a sheet, the sheet is prepared by uniformly applying a pressure of 15 MPa from above one main surface side of a sheet to be formed over 1 minute at a temperature of the melting point of the thermoplastic resin (A)+15° C., and in a cross-sectional surface in a thickness direction of the sheet, a region with a length of 0.125 mm and a thickness of 0.090 mm is subjected to image processing with a micrograph at a magnification of 2500:
(1) a total area of the magnetic particles (B) subjected to image processing is 40% to 65% of the area of the image processing region,
(2) a number of the magnetic particles (B) subjected to image processing is 200 to 500.
2 . The magnetic resin composition for injection molding according to claim 1 , wherein
the thermoplastic resin (A) comprises a polyamide resin.
3 . The magnetic resin composition for injection molding according to claim 1 , wherein
a silicon compound is deposited on at least a part of a surface layer of the magnetic particles (B).
4 . The magnetic resin composition for injection molding according to claim 1 , further comprising an antioxidant (D).
5 . The magnetic resin composition for injection molding according to claim 1 , further comprising a metal deactivator (E).
6 . The magnetic resin composition for injection molding according to claim 1 , further comprising a lubricant (C).
7 . An injection molded body for magnetic shields comprising a thermoplastic resin (A) that has a melting point of 100° C. to 400° C. and magnetic particles (B), comprising:
an injection molded body of a magnetic resin composition in which, as the magnetic particles (B), scale-like particles that are formed of an Fe—Si—Al alloy are used, and a mass ratio of the thermoplastic resin (A) to the Fe—Si—Al alloy, that is, thermoplastic resin (A)/Fe—Si—Al alloy is 10/90 to 15/85;
a sheet-like part provided at least at a part thereof; and
a surface that satisfies conditions (3) and (4) described below when a region with a length of 0.125 mm and a thickness of 0.090 mm is subjected to image processing with a micrograph at a magnification of 2500 in a cross-sectional surface in a thickness direction of the sheet-like part:
(3) a total area of the magnetic particles (B) subjected to image processing is 40% to 65% of the area of the image processing region,
(4) a number of the magnetic particles (B) subjected to image processing is 200 to 500.
8 . The injection molded body for magnetic shields according to claim 7 , wherein
a silicon compound is deposited on at least a part of a surface layer of the magnetic particles (B).
9 . The injection molded body for magnetic shields according to claim 7 , wherein
the thermoplastic resin (A) comprises a polyamide resin.
10 . The injection molded body for magnetic shields according to claim 7 , further comprising a lubricant (C).
11 . The injection molded body for magnetic shields according to claim 7 , wherein
the sheet-like part has an average thickness of 0.8 to 10 mm.
12 . An injection molded body for magnetic shields, which is formed by using the magnetic resin composition for injection molding according to claim 1 .