HOT MELT ADHESIVE COMPOSITION
The present invention relates to a pressure sensitive hot melt adhesive, particularly to a pressure sensitive hot melt positioning adhesive for use on feminine sanitary pads or adult incontinent products having improved peel values on fabrics made from Lyocell fibers, particularly eucalyptus-based Lyocell fibers.
1 - 18 . (canceled)
19 . A hot melt adhesive composition comprising, by total weight of the composition:
from 5 to 35% by weight of at least one styrene block polymeric component having an average hardness Shore A of 60 or less;
from 40 to 65% by weight of at least one tackifying resin;
from 15 to 40% by weight of at least one plasticizer; and
from 0 to 5% by weight of at least one stabilizer.
20 . A hot melt adhesive composition, according to claim 19 , wherein the at least one styrene block polymeric component has an average hardness Shore A of 50 or less.
21 . A hot melt adhesive composition, according to claim 19 , wherein the at least one stabilizer is in an amount of from 0 to 3% by weight, the hot melt adhesive composition further comprising from 0 to 5% of at least one additive, by total weight of the composition.
22 . A hot melt adhesive composition, according to claim 19 , wherein the polymeric component comprises, by total weight of the polymeric component:
from 25 to 100% by weight of at least one linear styrene block copolymer (a) having a styrene block content of 21% or less and a hardness Shore A of 45 or less;
from 0 to 75% by weight of at least one linear styrene block copolymer (b) having a styrene block content from 22% to 45%.
23 . A hot melt adhesive composition, according to claim 22 , wherein the average molecular weight (Mn) of each of linear styrene block copolymer(s) (a) and linear styrene block copolymer(s) (b) ranges from 70 000 g/mol to 170 000 g/mol.
24 . A hot melt adhesive composition, according to claim 22 , wherein the polymeric component comprises, by total weight of the polymeric component, from 35 to 100% of copolymer (a) and from 0 to 65% of copolymer (b).
25 . A hot melt adhesive composition, according to claim 22 , wherein the polymeric component comprises, by total weight of the polymeric component, from 25 to 95% of copolymer (a) and from 5 to 75% of copolymer (b).
26 . A hot melt adhesive composition, according to claim 22 , wherein the polymeric component consists of at least one copolymer (a).
27 . A hot melt adhesive composition, according to claim 22 , wherein the copolymer (a) is selected from the group consisting of SB, SI, SEB, SEP, SBBS, SBS, SEBS, SEPS, SEEPS, SIBS, SIS, random-block SBR, random-block SIR, and mixtures thereof.
28 . A hot melt adhesive composition, according to claim 27 , wherein at least one of the copolymer(s) (a) is a random-block SBR.
29 . A hot melt adhesive composition, according to claim 22 , wherein the copolymer (b) is selected from the group consisting of SB, SI, SEB, SEP, SBBS, SBS, SEBS, SEPS, SEEPS, SIBS, SIS, random-block SBR, random-block SIR, and mixtures thereof.
30 . A hot melt adhesive composition, according to claim 22 , wherein the polymeric composition is selected from the group consisting of:
from 60 to 70% of random-block SBR copolymer (a) and from 30 to 40% of SIS copolymer (b);
from 75 to 85% of random-block SBR copolymer (a) and from 15 to 25% of SIS copolymer (b);
from 30 to 40% of random-block SBR copolymer (a) and from 60 to 70% of SIS copolymer (b);
from 45 to 55% of random-block SBR copolymer (a) and 45 to 55% of SIS copolymer (b);
from 20 to 30% of random-block SBR copolymer (a) and from 70 to 80% of SIS copolymer (b);
from 60 to 70% of random-block SBR copolymer (a) and from 30 to 40% of SEBS copolymer (b);
from 60 to 70% of SIS copolymer (a) and from 30 to 40% of SIS copolymer (b);
from 60 to 70% of SIS copolymer (a) and from 30 to 40% of SEBS copolymer (b);
from 100% of SIS copolymer (a);
from 100% of random-block SBR polymer (a);
from 100% of a composition of copolymers (a) consisting of 60 to 70% of SIS copolymer (a) and from 30 to 40% of random-block SBR copolymer (a);
from 100% of a composition of copolymers (a) consisting of 45 to 55% of SIS copolymer (a) and from 45 to 55% of random-block SBR copolymer (a); and
from 27 to 37% of random-block SBR copolymer (a), from 27 to 37% of SIS copolymer (b) and from 30 to 40 of SEBS copolymer (b).
31 . A hot melt adhesive composition, according to claim 22 , wherein at least one of the copolymer(s) (a) is a random-block SBR.
32 . A hot melt adhesive composition, according to claim 19 , wherein the composition has a Brookfield viscosity at 163° C. from 500 to 8,000 mPa·s.
33 . A hot melt adhesive composition, according to claim 19 , characterized in that it does not comprise propylene-based polymer.
34 . Method of adhering a hygiene disposable article on a fabric comprising using the hot melt adhesive composition according to claim 19 .
35 . The method of claim 34 , wherein the hygiene disposable article is chosen from nonwoven hygiene disposable articles.
36 . The method of claim 34 , wherein the fabric is manufactured utilizing natural or synthetic fibers.