Method of manufacturing a hybrid dip cord having excellent fatigue resistance
View Patent ↗Provided is a method of manufacturing a hybrid dip cord, which includes: a step of preparing one nylon 6,6 yarn or nylon 6 yarn and one aramid yarn; a step of producing a primarily twisted yarn by applying a twist of 200 to 500 TPM by inputting one nylon 6,6 or nylon 6 yarn longer than the aramid yarn; a set of cabling the primarily twisted yarn as two to apply a twist of 200 to 500 TPM to thereby produce a raw cord; and a step of dipping the raw cord in an adhesive liquid and heat-treat the raw cord, in which the nylon 6,6 or nylon 6 is heat-shrunk so that the length of the nylon 6,6 or the nylon 6 becomes equal to the length of the aramid yarn.
1. A method of manufacturing a hybrid dip cord for a radial pneumatic tire, the method comprising:
a step of producing a primarily twisted yarn by applying the same twist number in the range of 200 to 500 TPM twist respectively to one nylon 6 , 6 yarn or nylon 6 yarn and one aramid yarn;
a step of producing a raw cord by applying 200 to 500 TPM twist by cabling the primarily twisted yarn as two yarns; and
a step of producing a dip cord by immersing the raw cord in a dipping solution and then heat-treating the raw cord to heat-shrink the nylon 6 , 6 yarn or the nylon 6 yarn so that the length of the nylon 6 , 6 yarn or the nylon 6 yarn is shorter than that of the aramid yarn
wherein the nylon 6 , 6 yarn or the nylon 6 yarn and the aramid yarn are pre-twisted and cabled simultaneously at a direct cabler,
wherein when the dip cord is untwisted, the aramid yarn is 10 to 30 mm/m longer than the nylon 6 , 6 yarn or nylon 6 yarn, and
wherein a strength of the dip cord is 24.7 kg to 37.2 kg.
2. The method of claim 1 , wherein the shrinking of the nylon 6 , 6 or nylon 6 yarns in the heat treatment step uses one selected from the group consisting of a method of controlling the tension applied to the raw cord, a method of adjusting the heat treatment temperature, and a method of controlling the heat treatment time.
3. The method of claim 2 , wherein the tension is controlled through a speed of a feed roller and a speed of a winding roller, the heat treatment temperature is 130 to 240° C., and the heat treatment time is 50 to 90 seconds.
4. The method of claim 1 , wherein the fineness of nylon 6 , 6 or nylon 6 yarn and aramid yarn is 500 to 3000 denier, respectively.