Method of making an osteoconductive fibrous article and a medical implant comprising such osteoconductive fibrous article
The disclosure relates to a method of making a bioceramic coating on a fibrous article for use in a medical implant, comprising steps of providing an article comprising fibers made from a biocompatible, non-biodegradable polymer; coating at least the fibers that will be in contact with bone upon use as an implant with a solution of a coating polymer to result in coated fibers having a coating polymer layer; treating the coated fibers with a dispersion of bioactive ceramic particles 0.01-10 μm in a treating solvent comprising a solvent for the coating polymer in at least one step; and substantially removing the treating solvent; to result in the particles being partly embedded in the coating polymer layer of the coated fibers.
1. A method of making a bioceramic coating on a fibrous article for use in a medical implant comprising the steps of:
a) providing an article comprising fibers made from a biocompatible, non-biodegradable polymer;
b) coating at least a portion of the fibers of the article with a dispersion or solution of a non-biodegradable coating polymer in a first solvent for the non-biodegradable coating polymer to result in coated fibers having a layer of non-biodegradable coating polymer;
c) treating the coated fibers by contacting the surface of the coated fibers by dip coating with a dispersion of bioactive ceramic particles of particle size 0.01-10 μm in a treating solvent comprising a second solvent for the non-biodegradable coating polymer in at least one step; and
d) removing the treating solvent to allow at least a portion of the bioactive ceramic particles to extend above the layer of the non-biodegradable coating polymer and increase the mass of the coated fibers of the article by 0.1-15 mass %, and wherein at least a portion of the layer of non-biodegradable coating polymer is exposed at the surface of the article.
2. The method according to claim 1 , wherein the fibrous article comprises fibers made from polyethylene terephthalate (PET).
3. The method according to claim 1 , wherein a solution of coating polymer is used for coating the fibers and the solution comprises 0.1-10 mass % of coating polymer.
4. The method according to claim 1 , wherein the non-biodegradable coating polymer is a thermoplastic elastomer and comprises a polyurethane block copolymer.
5. The method according to claim 4 , wherein the polyurethane block copolymer comprises an aliphatic polycarbonate as soft block.
6. The method according to claim 1 , wherein the bioactive ceramic particles comprise at least one of calcium phosphate and bioactive glass particles.
7. The method according to claim 6 , wherein the bioactive ceramic particles have a particle size of 0.1-6 μm.
8. The method according to claim 1 , wherein the bioactive ceramic particles comprise a mixture of calcium phosphate and bioactive glass particles.
9. The method according to claim 1 , wherein the dispersion is substantially free of dispersion aids and surfactants.
10. The method according to claim 9 , wherein the treating solvent further comprises a non-solvent for the non-biodegradable coating polymer, wherein the non-solvent for the coating polymer has a lower boiling point than the second solvent for the non-biodegradable coating polymer.
11. The method according to claim 1 , wherein the medical implant comprises an orthopedic implant.
12. The method according to claim 11 , wherein the orthopedic implant is a flexible tissue anchor, a cortical fixation device, an orthopedic suture, a bone cerclage cable, a synthetic tendon or ligament graft, an interspinous spacer or spinal disc prosthesis, a spinal fusion device, or a synthetic scaffold.
13. The method according to claim 11 , wherein the medical implant is configured to interface with bone.
14. The method according to claim 1 , further comprising the step of pretreating the article with a pre-wetting liquid comprising a solvent or a non-solvent for the coating polymer, wherein the pre-wetting liquid is a non-solvent for the biocompatible, non-biodegradable polymer.
15. The method according to claim 1 , wherein the particle dispersion is devoid of coating polymer.
16. The method according to claim 1 , wherein the first solvent is the same as the second solvent.
17. The method according to claim 1 , wherein the dip coating comprises at least two dip coating steps.
18. The method according to claim 1 , wherein the step of coating at least a portion of the fibers of the article with a dispersion or solution of a non-biodegradable coating polymer in a first solvent for the non-biodegradable coating polymer comprises a coating withdrawal rate from the dispersion or solution of 5 cm/sec or less.
19. The method according to claim 1 , wherein the fibrous article is a flexible tissue anchor, or a sleeve component thereof.
20. The method according to claim 1 , wherein the step of removing the treating solvent comprises evaporating the treating solvent.
21. The method according to claim 1 , wherein a plurality of the bioactive ceramic particles are embedded in the layer of non-biodegradable coating polymer after the step of removing the treating solvent.
22. The method according to claim 1 , wherein a plurality of bioactive ceramic particles are adhered to the layer of non-biodegradable coating polymer after the step of removing the treating solvent.