Granted Patent B2

US 12,313,553 · App. 18/158,140 · Granted May 27, 2025

Inventors: Abdulaziz Abdulrahman Al-Saadi (Dhahran, SA); Sathiyamoorthy Murugesan (Dhahran, SA); Muhammad Haroon (Dhahran, SA); Tawfik A. Saleh (Dhahran, SA)

Assignee: KING FAHD UNIVERSITY OF PETROLEUM AND MINERALS

G01N21/658B22F1/056B22F1/18B22F2301/255B22F2304/056B22F2304/058G01N2201/06113

Abstract

Claims (56)

1. A surface-enhanced Raman scattering (SERS) substrate, comprising:

a transparent substrate; and

a nanocomposite composition comprising:

a silver-loaded silica (Ag—SiO 2 ) nanocomposite having a silica core and a silver/silica shell disposed around the silica core; and

a zeolitic material having a nano porous structure;

wherein the silver/silica shell contains silver nanoparticles uniformly distributed therein;

wherein the Ag—SiO 2 nanocomposite is uniformly disposed on a surface of the zeolitic material;

wherein the nanoparticles of the Ag—SiO 2 nanocomposite are spherical and have a mean particle size of 100 to 500 nanometers (nm);

wherein the silver/silica shell of the Ag—SiO 2 nanocomposite has a mean thickness of 50 to 350 nm; and

wherein the SERS substrate has a specific surface area in a range of 150 to 300 m 2 /g, a cumulative specific pore volume in a range of 0.2 to 0.3 cm 3 /g, and an average pore diameter of 4 to 7 nm.

2. The SERS substrate of claim 1 , wherein the silica core of the Ag—SiO 2 nanocomposite has a mean diameter of 50 to 150 nm.

3. The SERS substrate of claim 1 , wherein the silver nanoparticles in the silver/silica shell of the Ag—SiO 2 nanocomposite have a mean particle size of 10 to 50 nm.

4. The SERS substrate of claim 1 , wherein the silver nanoparticles are at least one selected from the group consisting of nanospheres, nanorods, nanostars, nanotriangles, nanoprisms, nanocubes, nanofibers, nanoplates, nanowires, nanotetrahedrons, nanocrystals, nanohexagons, nanodisks, nanoribbons, nanocylinders, nanogranules, nanowhiskers, nanoflakes, nanofoils, nanopowders, nanoholes, nanobelts, nanourchins, nanoflowers, nanoislands, and nanomeshes.

5. The SERS substrate of claim 1 , wherein the Ag—SiO 2 nanocomposite has:

a specific surface area in a range of 10 to 100 square meter per gram (m 2 /g);

a cumulative specific pore volume in a range of 0.1 to 0.15 cubic centimeter per gram (cm 3 /g); and

an average pore diameter of 6 to 10 nm.

6. The SERS substrate of claim 1 , wherein the Ag—SiO 2 nanocomposite comprises from about 5 to 25 weight percentage (wt. %) of silver.

7. The SERS substrate of claim 1 , wherein a weight ratio of the silver-loaded silica nanocomposite to the zeolitic material in the nanocomposite ranges from about 1:5 to 5:1.

8. The SERS substrate of claim 1 , wherein the zeolitic material has a silicon-to-aluminum molar ratio of greater than 10:1.

9. The SERS substrate of claim 1 , wherein the zeolitic material has:

a specific surface area in a range of 300 to 400 m 2 /g;

a cumulative specific pore volume in a range of 0.15 to 0.2 cm 3 /g; and

an average pore diameter of 3 to 6 nm.

10. The SERS substrate of claim 1 , has a detection limit of 1x 10-9 molar (M) for a sulfur-containing compound.

11. The SERS substrate of claim 1 , wherein the transparent substrate comprises a glass substrate, and wherein the glass substrate is at least one selected from the group consisting of a fluorine doped tin oxide (FTO) coated glass substrate, a tin doped indium oxide (ITO) coated glass substrate, an aluminum doped zinc oxide (AZO) coated glass substrate, a niobium doped titanium dioxide (NTO) coated glass substrate, an indium doped cadmium oxide (ICO) coated glass substrate, an indium doped zinc oxide (IZO) coated glass substrate, a fluorine doped zinc oxide (FZO) coated glass substrate, a gallium doped zinc oxide (GZO) coated glass substrate, an antimony doped tin oxide (ATO) coated glass substrate, a phosphorus doped tin oxide (PTO) coated glass substrate, a zinc antimonate coated glass substrate, a zinc oxide coated glass substrate, a ruthenium oxide coated glass substrate, a rhenium oxide coated glass substrate, a silver oxide coated glass substrate, and a nickel oxide coated glass substrate.

12. A method of forming the SERS substrate of claim 1 , the method comprising:

preparing the nanocomposite composition by:

mixing a first silica precursor compound, an alcohol, and an ammonia solution to form a silica mixture;

sonicating a second silica precursor compound with the silica mixture and mixing to form a modified silica mixture;

dropwise adding a silver salt solution to the modified silica mixture and cooling to form a crude mixture containing a silver-loaded silica nanocomposite precipitate;

separating the silver-loaded silica nanocomposite precipitate from the crude mixture and drying to form the silver-loaded silica (Ag—SiO 2 ) nanocomposite;

calcinating a zeolitic precursor compound at a temperature of at least 500° C. to form the zeolitic material; and

mixing the silver-loaded silica nanocomposite with the zeolitic material to form the nanocomposite composition;

wherein a weight ratio of the silver-loaded silica nanocomposite to the zeolitic material in the nanocomposite composition ranges from about 1:5 to 5:1.

13. The method of claim 12 , wherein:

the first silica precursor compound comprises tetraethyl orthosilicate (TEOS), and tetramethyl orthosilicate (TMOS);

a volume ratio of the first silica precursor compound to the alcohol is in a range of 1:1 to 8:1; and

a volume ratio of the first silica precursor compound to the ammonia solution is in a range of 2:1 to 8:1;

wherein the alcohol has a formula (I)

wherein R 1 and R 2 are each independently selected from the group consisting of hydrogen, alkanes, alkenes, alkynes, cyclic alkanes, cyclic alkenes, cyclic alkynes and aromatics having in the range of 1 to 20 carbon atoms; and

wherein the ammonia solution has a concentration of 0.5 to 2 M.

14. The method of claim 12 , wherein:

the second silica precursor compound comprises alkoxysilane compound, wherein the alkoxysilane compound is at least one selected from the group consisting of trimethoxy(octadecyl)silane, octadecyltrichlorosilane and octyldimethylchlorosilane; and

a volume ratio of the first silica precursor compound to the second silica precursor compound is in a range of 1:3 to 3:1.

15. The method of claim 12 , wherein:

the silver salt is at least one salt selected from the group consisting of silver nitrate, silver sulfate, silver carbonate and silver chloride; and

the zeolitic precursor compound comprises ammonium zeolite having a silicon-to-aluminum molar ratio of greater than 10:1.

16. A method of obtaining a Raman spectrum of a sulfur-containing compound in a mixing composition, the method comprising:

contacting the mixing composition containing an analyte with the SERS substrate of claim 1 to form a sample;

exposing the sample to laser light such that a portion of the laser light is scattered by the sample to form scattered light; and

detecting the scattered light;

wherein the mixing composition comprises one or more hydrocarbons having boiling points less than 500° C.; and

wherein the sulfur-containing compound has a Raman scattering signal that is enhanced relative to that of the sulfur-containing compound in the absence of the SERS substrate.

17. The method of claim 16 , wherein the sulfur-containing compound comprises thiophene, dibenzothiophene (DBT), benzothiophene, 2-methylbenzothiophene, 2,4-dimethylthiophene, 3-methylthiophene, 2-methylthiophene, and/or a mixture thereof.

18. The method of claim 16 , wherein the laser light has a wavelength of 600 to 650 nm, and wherein the SERS substrate can detect the sulfur-containing compound with a detection limit of 1×10 −9 M.