Systems and methods for selective needling of fibrous preforms for shape-forming
A method for selective needling on a fibrous preform includes performing a through thickness reinforcement process on the fibrous preform and varying a needle density, a needle angle, and/or a needle penetrating depth during the through thickness reinforcement process such that a first needle density, a first needle angle, and/or a first needle penetrating depth of a first zone of the fibrous preform is greater than a second needle density, a second needle angle, and/or a second needle penetrating depth of a second zone of the fibrous preform. The method can further include identifying expected interlaminar stress throughout the fibrous preform and varying the needle density, needle angle, and/or needle penetrating depth in accordance with a magnitude of the expected interlaminar stress.
1. A method for selective needling on a fibrous preform, comprising:
shape forming the fibrous preform, including bending the fibrous preform about at least one axis to form a bent portion of the fibrous preform;
identifying a first zone on the fibrous preform, the first zone includes the bent portion of the fibrous preform;
identifying a second zone on the fibrous preform, the second zone excludes the bent portion of the fibrous preform;
performing a through thickness reinforcement process on the fibrous preform; and
varying a needle density during the through thickness reinforcement process such that a first needle density of the first zone is different from a second needle density of the second zone.
2. The method of claim 1 , wherein the first zone is identified as comprising a first expected interlaminar stress and the second zone is identified as comprising a second expected interlaminar stress, wherein the first expected interlaminar stress is different from the second expected interlaminar stress, and the first expected interlaminar stress and the second expected interlaminar stress are identified independent of the through thickness reinforcement process.
3. The method of claim 1 , further comprising varying a needle penetrating depth during the through thickness reinforcement process such that a first needle penetrating depth of at least one of the first zone or the second zone is different from a second needle penetrating depth of the other of the first zone or the second zone.
4. The method of claim 1 , further comprising varying a needle angle during the through thickness reinforcement process such that a first needle angle of at least one of the first zone or the second zone is different from a second needle angle of the other of the first zone or the second zone.
5. The method of claim 1 , wherein the through thickness reinforcement process comprises:
penetrating the fibrous preform with a first needle;
penetrating the fibrous preform with a second needle;
moving at least a portion of a first fiber from a first fabric layer of the fibrous preform into a second fabric layer of the fibrous preform in response to the first needle penetrating the fibrous preform; and
moving at least a portion of a second fiber from the first fabric layer of the fibrous preform into the second fabric layer of the fibrous preform in response to the second needle penetrating the fibrous preform.
6. The method of claim 1 , wherein the shape forming the fibrous preform is performed subsequent to the through thickness reinforcement process.
7. The method of claim 1 , wherein the shape forming the fibrous preform is performed prior to the through thickness reinforcement process.
8. The method of claim 1 , further comprising at least one of:
performing a compaction of the fibrous preform prior to performing the through-thickness reinforcement process; or
performing a heat-treatment process on the fibrous preform subsequent to performing the through thickness reinforcement process; or
performing a densification process on the fibrous preform subsequent to performing the through thickness reinforcement process.
9. The method of claim 1 , wherein the fibrous preform comprises a plurality of fabric layers, and the through thickness reinforcement process moves at least one through thickness reinforcement fiber from a first fabric layer of the fibrous preform into a second fabric layer of the fibrous preform, thereby interlocking the first fabric layer with the second fabric layer.
10. A method for selective needling on a fibrous preform, comprising:
shape forming the fibrous preform, including bending the fibrous preform about at least one axis to form a bent portion of the fibrous preform;
identifying a first zone on the fibrous preform, the first zone includes the bent portion of the fibrous preform;
identifying a second zone on the fibrous preform, the second zone excludes the bent portion of the fibrous preform;
performing a through thickness reinforcement process on the fibrous preform; and
varying a needle angle during the through thickness reinforcement process such that a first needle angle of the first zone is different from a second needle angle of the second zone.
11. The method of claim 10 , wherein the first zone is identified as comprising a first expected interlaminar stress and the second zone is identified as comprising a second expected interlaminar stress, wherein the first expected interlaminar stress is different from the second expected interlaminar stress, and the first expected interlaminar stress and the second expected interlaminar stress are identified independent of the through thickness reinforcement process.
12. The method of claim 11 , further comprising varying a needle penetrating depth during the through thickness reinforcement process such that a first needle penetrating depth of at least one of the first zone or the second zone is different from a second needle penetrating depth of the other of the first zone or the second zone.
13. The method of claim 10 , further comprising varying a needle density during the through thickness reinforcement process such that a first needle density of at least one of the first zone or the second zone is different from a second needle density of the other of the first zone or the second zone.
14. The method of claim 10 , wherein the through thickness reinforcement process comprises:
penetrating the fibrous preform with a first needle;
penetrating the fibrous preform with a second needle;
moving at least a portion of a first fiber from a first fabric layer of the fibrous preform into a second fabric layer of the fibrous preform in response to the first needle penetrating the fibrous preform; and
moving at least a portion of a second fiber from the first fabric layer of the fibrous preform into the second fabric layer of the fibrous preform in response to the second needle penetrating the fibrous preform.
15. The method of claim 10 , wherein the through thickness reinforcement process comprises:
penetrating a first fiber;
penetrating a second fiber; and
leaving a third fiber between the first fiber and the second fiber unneedled so as to maintain the third fiber as a continuous fiber.
16. The method of claim 10 , wherein the through thickness reinforcement process comprises penetrating a plurality of zones to generate a plurality of needled zones, wherein the plurality of needled zones comprise at least one of a triangular, a square, a hexagonal, or a curvilinear geometry.
17. The method of claim 10 , further comprising:
penetrating a first area of the fibrous preform with a first needling penetration penetrations pattern; and
penetrating a second area of the fibrous preform with a second needling penetration pattern,
wherein the first needling penetration pattern comprises at least one of a triangular pattern, a square pattern, a hexagonal pattern, or a curvilinear pattern, and
the second needling penetration pattern comprises another of the at least one of the triangular pattern, the square pattern, the hexagonal pattern, or the curvilinear pattern.
18. The method of claim 11 , wherein the needling angle is selected to correspond to a magnitude of the first expected interlaminar stress and the second expected interlaminar stress.
19. A method for selective needling on a fibrous preform, comprising:
identifying a first zone comprising a first expected interlaminar stress on the fibrous preform;
identifying a second zone comprising a second expected interlaminar stress different from the first expected interlaminar stress on the fibrous preform;
performing a through thickness reinforcement process on the fibrous preform; and
varying a needle penetrating depth during the through thickness reinforcement process such that a first needle penetrating depth of the first zone is different from a second needle penetrating depth of the second zone;
wherein the first expected interlaminar stress and the second expected interlaminar stress are identified independent of the through thickness reinforcement process.
20. The method of claim 19 , further comprising shape forming the fibrous preform, including bending the fibrous preform about at least one axis to form a bent portion of the fibrous preform;
the first zone includes the bent portion of the fibrous preform; and
the second zone excludes the bent portion of the fibrous preform.