Fuel cell electrode and fuel cell system including zirconium-based dopants
An electrode for a fuel cell system is provided. The electrode includes a carbon support. Platinum-based catalyst nanoparticles are dispersed on the carbon support. Zirconium-based dopants are disposed on the carbon support. In one example, a fuel cell system includes the electrode as a first electrode and further includes a second electrode and a fuel cell membrane. The fuel cell membrane is disposed between the first and second electrodes.
1 . An electrode for a fuel cell system, the electrode comprising:
a carbon support;
platinum-based catalyst nanoparticles dispersed on the carbon support; and
zirconium-based dopants disposed on the carbon support;
wherein the zirconium-based dopants comprise a first plurality of zirconium-based dopants that are dispersed on the carbon support between the platinum-based catalyst nanoparticles; and
wherein the zirconium-based dopants further comprise a second plurality of zirconium-based dopants that are dispersed on the platinum-based catalyst nanoparticles.
2 . The electrode of claim 1 , wherein the carbon support is a mesoporous carbon support having a plurality of pores formed therein with an average pore diameter of from about 2 to about 100 nm.
3 . The electrode of claim 1 , wherein the carbon support comprises carbon particles having an average particle size of from about 50 to about 800 nm.
4 . The electrode of claim 1 , wherein the platinum-based catalyst nanoparticles comprise platinum metal or a platinum alloy.
5 . The electrode of claim 1 , wherein the first plurality of zirconium-based dopants is chosen from zirconium atoms, zirconium oxide, zirconium carbide, or combinations thereof.
6 . The electrode of claim 5 , wherein the first plurality of zirconium-based dopants is chosen from zirconium oxide, zirconium carbide, or combinations thereof and has an average particle size of from about 1 to about 3 nm.
7 . The electrode of claim 1 , wherein the second plurality of zirconium-based dopants comprises zirconium oxide.
8 . The electrode of claim 1 , wherein the second plurality of zirconium-based dopants has an average particle size of from about 0.1 to about 1 nm.
9 . The electrode of claim 1 , wherein the carbon support, the platinum-based catalyst nanoparticles, and the zirconium-based dopants together define a catalyst layer, and wherein the zirconium-based dopants are present in the catalyst layer in an amount of from about 0.50 to about 3.0 wt. %, based on the weight of the carbon support.
10 . The electrode of claim 1 , wherein the carbon support, the platinum-based catalyst nanoparticles, and the zirconium-based dopants together define a catalyst layer, and wherein the platinum-based catalyst nanoparticles are present in the catalyst layer in an amount of from about 30 to about 50 wt. %, based on the weight of the carbon support.
11 . The electrode of claim 1 , wherein the platinum-based catalyst nanoparticles have an average particle size of from about 1.5 to about 4.0 nm.
12 . The electrode of claim 1 , wherein the carbon support is free of nitrogen.
13 . A fuel cell system comprising:
a first electrode;
a second electrode comprising:
a carbon support;
platinum-based catalyst nanoparticles dispersed on the carbon support; and
zirconium-based dopants disposed on the carbon support;
wherein the zirconium-based dopants comprise a first plurality of zirconium-based dopants that are dispersed on the carbon support between the platinum-based catalyst nanoparticles; and
wherein the zirconium-based dopants further comprise a second plurality of zirconium-based dopants that are dispersed on the platinum-based catalyst nanoparticles; and
a fuel cell membrane disposed between the first and second electrodes.
14 . The fuel cell system of claim 13 , wherein the first plurality of zirconium-based dopants is chosen from zirconium atoms, zirconium oxide, zirconium carbide, or combinations thereof.
15 . The fuel cell system of claim 13 , wherein the second plurality of zirconium-based dopants comprises zirconium oxide.
16 . A method for making an electrode for a fuel cell system, the method comprising:
combining an organic carbon-forming precursor, a zirconium salt dopant-forming precursor, and a pore-forming agent to form a precursor mixture;
converting the precursor mixture to a zirconium-doped carbon support; and
dispersing platinum-based catalyst nanoparticles on the zirconium-doped carbon support.
17 . The method of claim 16 , wherein converting comprises:
heat treating the precursor mixture at first processing conditions to pyrolyze the organic carbon-forming precursor and the zirconium salt dopant-forming precursor to form the zirconium-doped carbon support that includes zirconium-based dopants and that has pores formed therein defined by the pore-forming agent; and
removing the pore-forming agent from the pores of the zirconium-doped carbon support.
18 . The method of claim 17 , wherein heat treating the precursor mixture at the first processing conditions includes exposing the precursor mixture to a temperature of from about 800 to about 1500° C. for a time of from about 30 seconds to about 4 hours.
19 . The method of claim 17 , further comprising:
optionally depositing additional zirconium-based dopants on the zirconium-doped carbon support; and
heat treating the zirconium-doped carbon support at second processing conditions to arrange a portion of the zirconium-based dopants on the platinum-based catalyst nanoparticles after removing the pore-forming agent from the pores of the zirconium-doped carbon support.
20 . The method of claim 19 , wherein heat treating the zirconium-doped carbon support at the second processing conditions includes exposing the zirconium-doped carbon support to a temperature of from about 300 to about 1000° C. for a time of from about 30 seconds to about 4 hours.