Multilayer corrosion system
An article including a substrate having on at least a portion of its surface a multilayer coating. The multilayer coating including at least one layer of electroless nickel overlying the portion of the surface, at least one layer of electrolytic nickel overlying the layer of electroless nickel, and at least one layer of an electrolytic tin-nickel overlying the layer of electrolytic nickel.
1. An article comprising:
a metal substrate, which is optionally zincate coated, having on at least a portion of its surface a multilayer coating, the multilayer coating comprising at least one layer of electroless nickel overlying the portion of the surface, at least one layer of electrolytic nickel overlying the layer of electroless nickel, and at least one layer of electrolytic tin-nickel overlying the layer of electrolytic nickel;
wherein the at least one layer of electroless nickel has a thickness of about 0.5 mil to about 2 mil; and
wherein the thickness of the at least one layer of electrolytic nickel is at least 10% less than the thickness of the at least one layer of electroless nickel.
2. The article of claim 1 , wherein the at least one layer of electroless nickel has a phosphorous content of about 5% to about 14% by weight.
3. The article of claim 1 , wherein the at least one layer of electroless nickel comprises two electroless nickel layers having different phosphorous contents.
4. The article of claim 1 , wherein the at least one layer of electroless nickel is microporous and the layer of electrolytic nickel is pore free or substantially pore free.
5. The article of claim 1 , wherein the layer of electrolytic tin-nickel alloy includes about 50% to about 80% by weight tin, with the balance being substantially nickel.
6. The article of claim 1 , wherein the layer of electrolytic nickel has a thickness of about 0.05 mils to about 0.6 mils.
7. The article of claim 1 , wherein the layer of electrolytic tin-nickel alloy has a thickness of about 0.1 mils to about 0.6 mils.
8. The article of claim 1 , wherein the metal substrate is zincated with a zincate immersion coating.
9. The article of claim 1 , wherein the multilayer coating has a thickness of about 0.5 mils to about 2.0 mils and is able to withstand at least 336 hours of neutral salt spray corrosion testing (NSST) without corrosion of the underlying substrate.
10. The article of claim 1 , wherein the metal substrate comprises an aluminum substrate.
11. The article of claim 3 , wherein a first electroless nickel layer has a phosphorous content of about 5% to about 9% by weight, and a second electroless nickel layer has a phosphorous content of about 10% to about 14% by weight.