Composition for a water permeable court surface and method for production of same
A water permeable court surface comprises a porous substrate ( 5 ) on which there is a porous rubber shock layer ( 3 ) on which is at least one layer ( 1,2 ) of an acrylic composition, wherein the acrylic composition comprises a two pack water based polyurethane.
1 . A composite for a water permeable court surface which comprises a porous substrate on which there is a porous rubber shock layer on which is at least one layer of an acrylic composition, wherein the acrylic composition comprises a two part water based polyurethane and wherein the acrylic composition comprises a first component which comprises an organic solvent-free aqueous dispersion of a copolymer based on an aliphatic polycarbonate polyurethane and a polyacrylate.
2 . The composite according to claim 1 , wherein the first component is blended with a second component, which is a water miscible polyiscocyanate.
3 . The composite of claim 2 , wherein the first component and the second component are blended with a water based acrylic.
4 . The composite of claim 1 , wherein the porous substrate is of a bituminous or tar derived material.
5 . The composite of claim 1 , wherein the rubber shock layer is formed of rubber granules bonded together by a polyurethane binder.
6 . The composite of claim 5 , wherein the rubber granules have a granule size having a diameter of from about 1 to about 3 mm.
7 . The composite of claim 1 , wherein the rubber shock layer has a thickness of about 4 mm to about 6 mm.
8 . The composite of claim 1 , wherein the rubber shock layer is fixed to the substrate by means of an adhesive.
9 . The composite of claim 8 , wherein the adhesive is a two part polyurethane adhesive.
10 . The composite of claim 8 , wherein the adhesive is applied in the form of beads.
11 . The composite of claim 10 , wherein a gap is provided between the beads of adhesive are about 10 mm wide.
12 . The composite of claim 1 , wherein the rubber shock layer is treated with a detergent.
13 . The composite of claim 12 , wherein the detergent comprises a blend of sodium metasilicate, anionic and non-ionic surfactants, sequestering agent, solubiliser and glycol ether.
14 . The composite of claim 1 , wherein the acrylic composition is spray applied in two applications.
15 . The composite of claim 14 , wherein the acrylic composition applied in a first application contains about 20% to about 30% acrylic by weight.
16 . The composite of claim 14 , wherein a final coat comprises about 40% to about 50% acrylic by weight.
17 . A method for production of the composite of claim 1 for a water permeable court surface which comprises the steps of providing a porous substrate, providing a porous rubber shock layer on top of the porous substrate and providing at least one layer of acrylic composition on top of the porous rubber shock layer, wherein the acrylic composition comprises a two pack water based polyurethane.
18 . The method of claim 17 , wherein the method comprises the step of fixing a rubber shock layer to the substrate by means of an adhesive.
19 . The method of claim 18 , wherein the method comprises the step of applying adhesive in bead form whereby beads of glue are formed in substantially parallel lines with gaps in between to allow water to pass therethrough.
20 . The method of claim 18 , wherein the method does not include the step of applying adhesive by means of dot gluing.
21 . The method of claim 17 , wherein the method comprises the step of treating the rubber shock layer with a detergent.
22 . The method of claim 17 , wherein the method includes the step of blending the two part water based polyurethane with an acrylic resin.
23 . The method of claim 17 , wherein the method includes the step of applying the acrylic composition by spraying.
24 . The method of claim 17 , wherein the step of applying the acrylic composition is applied in two applications.