THREE-WAY CATALYST HAVING LOW NH3 FORMATION AND PREPARATION METHOD THEREFOR
A three-way catalyst having low NH 3 formation is disclosed. The catalyst includes a carrier and a coating material. The coating material includes a precious metal active component and a catalytic material. The precious metal active component includes a first precious metal active component and a second precious metal active component. The first precious metal active component is a composition containing Ru. The second precious metal active component is a composition containing Pt, Pd and Rh. Alternatively, the second precious metal active component is a composition containing Pd and Rh.
1 . A three-way catalyst, comprising a carrier and a coating material, the coating material comprising a precious metal active component and a catalytic material, wherein:
the precious metal active component includes a first precious metal active component and a second precious metal active component;
the first precious metal active component comprises Ru; and
the second precious metal active component comprises Pd and Rh, and optionally, Pt.
2 . The three-way catalyst according to claim 1 , wherein the Ru is present in the first precious metal active component in an amount of 1 ~ 100 g/ft 3 .
3 . The three-way catalyst according to claim 2 , wherein the Ru is present in the first precious metal active component in an amount of 5 ~ 40 g/ft 3 .
4 . The three-way catalyst according to claim 1 , wherein the Ru in the first precious metal active component contains metallic ruthenium and/or ruthenium oxide.
5 . The three-way catalyst according to claim 1 , wherein the catalytic material comprises an oxygen storage material and an alumina material.
6 . The three-way catalyst according to claim 5 , wherein the oxygen storage material comprises CeO 2 , CeO 2 —ZrO 2 , CeO 2 —ZrO 2 —Y 2 O 3 , CeO 2 —ZrO 2 —La 2 O 3 —Y 2 O 3 , CeO 2 —ZrO 2 —La 2 O 3 —Pr 2 O 3 , or CeO 2 —ZrO 2 —La 2 O 3 —La 2 O 3 .
7 . The three-way catalyst according to claim 5 , wherein the alumina material comprises pure alumina or a modified alumina containing La and/or Ce.
8 . The three-way catalyst according to claim 1 , wherein the carrier comprises a ceramic carrier or a metal carrier.
9 . A method for preparing the three-way catalyst according to claim 1 , comprising:
loading a first salt solution of the first precious metal active component and a second salt solution of the second precious metal active component onto a catalytic material;
drying and calcining the catalytic material with the first and second salt solutions loaded thereon to obtain a coating material;
mixing the coating material, water, and a binder to obtain a coating material slurry;
coating the coating material slurry on the carrier; and
drying and calcining the carrier with the coating material slurry thereon to obtain the three-way catalyst.