BIODEGRADABLE POLYESTER RESIN COMPOSITION AND BIODEGRADABLE MOLDED ARTICLE INCLUDING BIODEGRADABLE POLYESTER RESIN COMPOSITION

1 . A biodegradable polyester resin composition, comprising: a polyester resin comprising a diol, an aromatic dicarboxylic acid and an aliphatic dicarboxylic acid,

wherein a first weight swelling rate of the biodegradable polyester resin composition ranges from 4% to 20%,

wherein the first weight swelling rate is measured by a measurement method below:

wherein in the measurement method

the biodegradable polyester resin composition is dried at 80° C., placed in a stainless steel mold, and compressed at 210° C. under a pressure of 10 MPa for 3 minutes to produce a polyester sheet having a thickness of 300 μm, an initial weight of the polyester sheet and a weight of the polyester sheet after being immersed in room-temperature ethanol for 2 hours are measured, and the first weight swelling rate is obtained by dividing a difference between the weight of the polyester sheet after being immersed and the initial weight by the initial weight.

2 . The biodegradable polyester resin composition according to claim 1 , wherein a volume swelling rate of the biodegradable polyester resin composition ranges from 5% to 20%,

wherein the volume swelling rate is measured by a measurement method below:

wherein in the measurement method

an initial volume of the polyester sheet and a volume of the polyester sheet after being immersed in room-temperature ethanol for 2 hours are measured, and the volume swelling rate is obtained by dividing a difference between the volume of the polyester sheet after being immersed and the initial volume by the initial volume.

3 . The biodegradable polyester resin composition according to claim 1 , wherein a content of a silicon element in the biodegradable polyester resin composition ranges from 0.1 ppm to 1000 ppm.

4 . The biodegradable polyester resin composition according to claim 1 , wherein a water contact angle of a surface of the polyester sheet ranges from 45° to 85°.

5 . The biodegradable polyester resin composition according to claim 4 , wherein a polarity of the surface of the polyester sheet ranges from 3 mN/m to 5 mN/m.

6 . The biodegradable polyester resin composition according to claim 3 , further comprising a metal.

7 . The biodegradable polyester resin composition according to claim 6 , wherein the metal comprises an iron element,

wherein a ratio of the iron element relative to the silicon element ranges from 0.1 to 0.7.

8 . The biodegradable polyester resin composition according to claim 1 , wherein a hydrolysis degree after one week of the biodegradable polyester resin composition ranges from 35% to 60%, and

a hydrolysis degree after three weeks of the biodegradable polyester resin composition is 85% or more,

wherein the hydrolysis degree after one week and the hydrolysis degree after three weeks are measured by a measurement method below:

wherein in the measurement method

the hydrolysis degree after one week is a number average molecular weight reduction rate of the biodegradable polyester resin composition placed for one week under high-temperature and high-humidity conditions of 80° C. and a humidity of 100%, compared to an initial number average molecular weight of the biodegradable polyester resin composition, and

the hydrolysis degree after three weeks is a number average molecular weight reduction rate of the biodegradable polyester resin composition placed for three weeks under high-temperature and high-humidity conditions of 80° C. and a humidity of 100%, compared to an initial number average molecular weight of the biodegradable polyester resin composition.

9 . The biodegradable polyester resin composition according to claim 1 , wherein a second weight swelling rate of the biodegradable polyester resin composition ranges from 4% to 20%,

wherein the second weight swelling rate is measured by a measurement method below:

wherein in the measurement method an initial weight of the polyester sheet and a weight of the polyester sheet after being immersed in room-temperature ethanol for 24 hours are measured, and the second weight swelling rate is obtained by dividing a difference between the weight of the polyester sheet after being immersed and the initial weight by the initial weight.

10 . The biodegradable polyester resin composition according to claim 9 , wherein a difference between the first weight swelling rate and the second swelling rate is 5% or less.

11 . A biodegradable polyester resin composition, comprising a polyester resin comprising a diol, an aromatic dicarboxylic acid and an aliphatic dicarboxylic acid,

wherein a wet hardness reduction rate of the biodegradable polyester resin composition is 15% or less,

wherein the wet hardness reduction rate is measured by a measurement method below:

wherein in the measurement method the biodegradable polyester resin composition is used to manufacture a polyester block having a thickness of 2.5 mm, an initial hardness of the polyester block and a wet hardness of the polyester block after being immersed in water at 30° C. for 24 hours are measured, and the wet hardness reduction rate is obtained by dividing a difference between the initial hardness and the wet hardness by the initial hardness.

12 . The biodegradable polyester resin composition according to claim 11 , wherein the initial hardness is a Shore D hardness ranging from 30 to 45, and

the wet hardness is a Shore D hardness ranging from 28 to 43.

13 . The biodegradable polyester resin composition according to claim 11 , wherein the wet hardness reduction rate is 12% or less.

14 . The biodegradable polyester resin composition according to claim 11 , wherein a content of a silicon element in the biodegradable polyester resin composition ranges from 0.1 ppm to 1000 ppm.

15 . The biodegradable polyester resin composition according to claim 11 , wherein a water contact angle of a surface of the polyester block ranges from 45° to 85°.

16 . The biodegradable polyester resin composition according to claim 11 , wherein a difference between the wet hardness after being immersed in 30° C. water for 1 hour and the wet hardness after being immersed in 30° C. water for 24 hours is 10% or less based on the initial hardness.

17 . The biodegradable polyester resin composition according to claim 11 , wherein a difference between the wet hardness after being immersed in 30° C. water for 24 hours and a wet hardness after being immersed in 70° C. water for 24 hours is 10% or less based on the initial hardness.

18 . A biodegradable molded article, comprising: a polyester resin comprising a diol, an aromatic dicarboxylic acid and an aliphatic dicarboxylic acid,

wherein a weight swelling rate of the biodegradable molded article ranges from 4% to 20%,

wherein the weight swelling rate is measured by a measurement method below:

wherein in the measurement method

the molded article is manufactured into a sample having a thickness of 300 μm, an initial weight of the sample and a weight of the sample after being immersed in room-temperature ethanol for 2 hours are measured, and the weight swelling rate is obtained by dividing a difference between the weight of the sample after being immersed and the initial weight by the initial weight.

19 . The biodegradable molded article according to claim 18 , wherein a wet hardness reduction rate of the biodegradable molded article is 15% or less,

wherein the wet hardness reduction rate is measured by a measurement method below:

wherein in the measurement method the biodegradable molded article is processed into a block having a thickness of 2.5 mm, an initial hardness of the block and a wet hardness of the block after being immersed in 30° C. water for 24 hours are measured, and the wet hardness reduction rate is obtained by dividing a difference between the initial hardness and the wet hardness by the initial hardness.

20 . The biodegradable molded article according to claim 19 , comprising an iron element and a silicon element,

wherein a mass ratio of the iron element relative to the silicon element ranges from 0.1 to 0.7.