ONE-COMPONENT SYSTEM COMPRISING BLOCKED POLYURETHANE PREPOLYMERS
The present invention relates to a one-component system comprising a) at least one polyurethane prepolymer based on at least one di- and/or polyisocyanate and at least one di- and/or polyol, wherein at least one di- or polyol is a polyalkylene glycol having a number-average molecular weight of 900 to 2150 g/mol, wherein all unconverted isocyanate groups are blocked with at least one malonic ester and b) at least one di and/or polyamine; to a process for its production, to its use and to processes employing it for producing artificial leather and (artificial) leather coatings.
1 . A one-component system comprising
a) at least one polyurethane prepolymer based on at least one di- and/or polyisocyanate and at least one di- and/or polyol,
wherein at least one di- or polyol is a polyalkylene glycol having a number-average molecular weight of 900 to 2150 g/mol, wherein all unconverted isocyanate groups are blocked with at least one malonic ester, and
b) at least one di- and/or polyamine.
2 . The one-component system according to claim 1 , wherein the prepolymer is based on a diisocyanate.
3 . The one-component system according to claim 2 , wherein the diisocyanate comprises a (cyclo)aliphatic diisocyanate.
4 . The one-component system according to claim 2 , wherein the diisocyanate is selected from HDI, TMDI, H12MDI, IPDI, TMXDI, XDI, MDI and TDI.
5 . The one-component system according to claim 4 , wherein the diisocyanate comprises IPDI.
6 . The one-component system according to claim 1 , wherein the prepolymer is based on one or two diols.
7 . The one-component system according to claim 6 , wherein the prepolymer is based on 80-100% by weight of a first diol and 0-20% by weight of a second diol, wherein the % by weights are based on the total mass of diols.
8 . The one-component system according to claim 1 , wherein the polyalkylene glycol is a polytetramethylene ether glycol.
9 . The one-component system according to claim 8 , wherein the number-average molecular weight of the polytetramethylene ether glycol is 950-1200 g/mol.
10 . The one-component system according to claim 7 , wherein the second diol is a hydrocarbon diol having two to ten carbon atoms.
11 . The one-component system according to claim 10 , wherein the hydrocarbon diol is selected from the group consisting of ethylene glycol, n-propylene glycol, i-propane glycol, 2-methyl-1,3-propanediol, n-butylene glycol, n-pentyl glycol, n-hexanediol, diethylene glycol, 1,4-cyclohexanedimethanol, tripropylene glycol and 1,10-decanediol.
12 . The one-component system according to claim 1 , wherein the at least one malonic ester is selected from dimethyl malonate, diethyl malonate, diisopropyl malonate and monoethyl malonate.
13 . The one-component system according to claim 12 , wherein the malonic ester is diethyl malonate.
14 . The one-component system according to claim 1 , wherein the di-/polyamine is a diamine selected from the group consisting of isophorondiamine, 4,4′-diaminodicyclohexylmethane, 4,4′-methylenebis(2-methylcyclohexanamine), a mixture of 2,2,4- and 2,4,4-trimethylhexamethylenediamine, hexanediamine, 1,3-bis(aminomethyl)cyclohexane and a polyoxypropylenediamine.
15 . The use of a one-component system according to claim 1 for producing artificial leathers or (artificial) leather coatings.
16 . A process for producing a one-component system according to claim 1 , the process comprising mixing at least one polyurethane prepolymer based on a polyalkylene glycol having a number-average molecular weight of 900 to 2150 g/mol, wherein all unconverted isocyanate groups of the polyurethane prepolymer are blocked with at least one malonic ester, and at least one di- and/or polyamine.
17 . A process for producing an artificial leather, wherein the one-component system according to claim 1 is applied to a carrier and thermally cured.
18 . A process for producing an artificial leather coating, wherein the one-component system according to claim 1 is applied to a piece of artificial leather or leather and thermally cured.