Material for plasma spray comprising Y—O—F compound, method for producing the same, and spray coating prepared using the same
Disclosed are a material for spray for plasma spray coating having high plasma resistance and a method for producing the same. The material for plasma spray comprises an yttrium compound, and the numbers of moles of Y (yttrium), O (oxygen), and F (fluorine) in the yttrium compound satisfy 1.5<(O+F)/Y<2.0.
1. A material for plasma spray comprising an yttrium compound, wherein the numbers of moles of Y (yttrium), O (oxygen), and F (fluorine) in the yttrium compound satisfy 1.5<(O+F)/Y<2.0,
wherein the yttrium compound comprises a Y—O—F compound and Y 2 O 3 , and
wherein the Y—O—F compound comprises a first Y—O—F compound with O/F=1 and a second Y—O—F compound with O/F<1, wherein the content of Y 2 O 3 is 15-25 wt %.
2. The material for plasma spray of claim 1 , wherein the second Y—O—F compound includes at least one compound selected from the group consisting of Y 4 O 3 F 6 , Y 5 O 4 F 7 , Y 6 O 5 F 8 , and Y 7 O 6 O 9 .
3. The material for plasma spray of claim 1 , wherein the second Y—O—F compound includes Y 5 O 4 F 7 .
4. The material for plasma spray of claim 1 , wherein a content % by weight of the second Y—O—F compound is lower than a content % by weight of the first Y—O—F compound.
5. A plasma spray coating comprising an yttrium compound, wherein the numbers of moles of Y, O, and F in the yttrium compound satisfy 1.6<(O+F)/Y<1.9 and the porosity of the plasma spray coating is 3% or less,
wherein the yttrium compound comprises YOF and Y 2 O 3 , and
wherein a content % by weight of Y 2 O 3 is more than a content % by weight of YOF.