Three-Dimensional Thin Film Structure Having Microparticles Enclosed Therein And Method For Manufacturing Same
A three-dimensional structure including a polymer film having a plurality of layers, wherein a microparticle is encapsulated in an internal space of the three-dimensional structure and each layer of the polymer film having the plurality of layers has mechanical strengths different from each other.
1 .- 9 . (canceled)
10 . A biological tissue-like structure comprising:
a polymer film having a plurality of layers, wherein a cell is encapsulated in an internal space of said structure, and each layer of the polymer film having the plurality of layers has mechanical strengths different from each other;
a second cell existing outside the three-dimensional structure;
wherein the cell encapsulated in the structure forms a structure extending to an outside of the structure, and
an intercellular interaction is able to occur between the cell encapsulated in the structure and the second cell existing outside the structure.
11 . A method for producing a three-dimensional structure encapsulating a microparticle,
the method comprising the steps of:
(a) forming a polymer film having a plurality of layers
(b) floating the microparticle over a surface of the polymer film having the plurality of layers and
(c) generating a stress distribution in a thickness direction in the polymer film having the plurality of layers to form a three-dimensional structure in a self-assembling manner in the polymer film having the plurality of layers.
12 . The method for producing a three-dimensional structure according to claim 11 , further comprising a step of forming a sacrificial layer on a substrate,
wherein the step (a) is a step of laminating polymer materials having swelling ratios different from each other on the sacrificial layer to form the polymer film having the plurality of layers;
the step (b) is a step of adding a suspension containing the microparticle to the polymer film having the plurality of layers and the step (c) is a step of decomposing the sacrificial layer, thereby releasing the polymer film from the substrate.
13 . (canceled)
14 . The method for producing a three-dimensional structure according to claim 11 , further comprising a step of forming a layer composed of an extracellular matrix on a surface of the polymer film.
15 . The method for producing a three-dimensional structure according to claim 11 , wherein the polymer film has a thickness of 15 to 400 nm.
16 . A laminate comprising:
a substrate;
a sacrificial layer laminated on the substrate; and
a polymer film having a plurality of layers laminated on the sacrificial layer,
wherein each layer of the polymer film having the plurality of layers is composed of a polymer material that may generate a stress distribution in a thickness direction in the polymer film when the polymer film is released from the substrate by decomposing the sacrificial layer.
17 . The laminate according to claim 16 , wherein each layer of the polymer film having the plurality of layers is composed of a polymer material having swelling ratios different from each other.
18 . The laminate according to claim 16 , further comprising a layer composed of an extracellular matrix laminated on the polymer film.
19 . The laminate according to claim 16 , wherein the polymer film has a thickness of 15 to 400 nm.