Selective Deposition of Thin Films with Improved Stability
A method of processing a substrate is disclosed which includes depositing a layer in a processing chamber on a field region, a sidewall region, and a fill region of a feature of the substrate, wherein a hardness of a portion of the layer deposited on the sidewall region is lower than a hardness of a portion of the layer deposited on the field region, and lower than a hardness of a portion of the layer deposited on the fill region.
1 . A method of processing a substrate, comprising:
depositing a layer in a processing chamber on a field region, a sidewall region, and a fill region of a feature of the substrate, wherein a hardness of a portion of the layer deposited on the sidewall region is lower than a hardness of a portion of the layer deposited on the field region, and lower than a hardness of a portion of the layer deposited on the fill region.
2 . The method of claim 1 , wherein the layer is silicon, silicon oxide, silicon nitride, or silicon carbon nitride.
3 . The method of claim 1 , wherein the layer further comprises phosphorus, boron, fluorine, aluminum, nitrogen, or a combination thereof.
4 . The method of claim 1 , wherein the portion of the layer deposited on the sidewall region has a Young's modulus which is at least about 10% lower than a Young's modulus of the portion of the layer deposited on the field region and the portion of the layer deposited on the fill region.
5 . The method of claim 1 , wherein the layer is deposited via plasma enhanced chemical vapor deposition (PECVD) or chemical vapor deposition (CVD).
6 . The method of claim 5 , wherein the layer is deposited utilizing a chemical precursor comprising tetraethyl orthosilicate, octamethylcyclotetrasiloxane, silane, or a combination thereof.
7 . The method of claim 6 , wherein a flow rate of the chemical precursor into the processing chamber is from about 0.1 to 5 grams/min.
8 . The method of claim 6 , wherein the layer is deposited utilizing a dopant chemical precursor comprising phosphorus, boron, fluorine, aluminum, or a combination thereof.
9 . The method of claim 8 , wherein the dopant chemical precursor is provided into the processing chamber at a flow rate from about 0.1 to 2 grams/minute.
10 . The method of claim 6 , further comprising diluting the chemical precursor in a carrier gas comprising Ar, He, Hz, or a combination thereof.
11 . The method of claim 10 , wherein the carrier gas is provided into the processing chamber at a flow rate from about 1 to 100 slm.
12 . The method of claim 6 , wherein the layer is deposited utilizing an oxygen precursor of diatomic oxygen, ozone, nitrous oxide, or a combination thereof, and wherein the oxygen precursor is provided into the processing chamber at a flow rate from about 1 to 50 slm.
13 . The method of claim 5 , wherein the plasma enhanced chemical vapor deposition comprises a dual frequency RF bias comprising a low frequency RF signal having a frequency of about 200 kHz to 600 kHz, and a high frequency RF signal having a frequency of about 2 MHz to 100 MHz.
14 . The method of claim 13 , wherein a power of the low frequency RF signal and a power of the high frequency RF signal are each individually from about 50 watts to about 5000 watts.
15 . The method of claim 13 , wherein a ratio of a power of the low frequency RF signal to a power of the high frequency RF signal is greater than 1.
16 . The method of claim 13 , wherein one of the high frequency RF signal or the low frequency RF signal is applied to a showerhead configured to flow gases into the processing chamber, and the other is applied to a substrate support configured to support the substrate during the processing.
17 . The method of claim 16 , wherein a spacing between a showerhead of the processing chamber and the substrate support is from about 50 mils to 1500 mils.
18 . The method of claim 1 , wherein a temperature of the substrate is from about 50° C. to about 500° C.
19 . The method of claim 1 , wherein a pressure within the processing chamber is from about 0.1 torr to about 10 torr.
20 . A method of processing a substrate, comprising:
depositing a layer on a field region, a sidewall region, and a fill region of a feature of the substrate, wherein a hardness of a portion of the layer deposited on the sidewall region is lower than a hardness of a portion of the layer deposited on the field region, and lower than a hardness of a portion of the layer deposited on the fill region; and
reducing a thickness of at least a portion of the substrate via chemical mechanical planarization to form a processed substrate, wherein the portion of the layer on the sidewall region of the processed substrate is free from cracks.