Recyclable film for thermoforming
Recyclable films having a first layer containing a polyethylene, a second layer containing a high-density polyethylene and a hydrocarbon resin, and a third layer containing a polyethylene may be used for thermoforming packaging components. Both the first and third layers have an overall density between about 0.92 g/cm 3 and 0.97 g/cm 3 . The film structure is advantageous as it can be more easily thermoformed than traditional high-density polyethylene films and can maintain the shape taken during thermoforming, exhibiting minimal warping or shrinking.
1. A thermoformable base film comprising:
a first layer comprising at least one polyethylene and having an overall density between about 0.92 g/cm 3 and 0.97 g/cm 3 ,
multiple second layers, each comprising a high-density polyethylene and a hydrocarbon resin, and
a third layer comprising at least one polyethylene and having an overall density between about 0.92 g/cm 3 and 0.97 g/cm 3 ,
wherein the multiple second layers are located between the first layer and the third layer, and wherein after thermoforming, the thermoformable base film maintains a shape taken during thermoforming.
2. The thermoformable base film according to claim 1 , wherein the multiple second layers are separated by other layers.
3. The thermoformable base film according to claim 1 , further comprising a fourth layer comprising a high-density polyethylene and an inorganic particle, wherein the inorganic particle is present in the fourth layer at a level of at least 5% by weight and wherein the fourth layer is between the first layer and the third layer.
4. The thermoformable base film according to claim 3 , wherein the inorganic particle is calcium carbonate.
5. The thermoformable base film according to claim 1 , wherein the first layer comprises a blend of high-density polyethylene and a polyethylene having a density less than 0.93 g/cm 3 .
6. The thermoformable base film according to claim 1 , wherein the first layer and the third layer each form a surface of the thermoformable base film.
7. The thermoformable base film according to claim 1 , further comprising an oxygen barrier layer comprising an ethylene vinyl alcohol copolymer, wherein the oxygen barrier layer is located between the first layer and the third layer.
8. The thermoformable base film according to claim 1 , wherein the hydrocarbon resin is present from 5% to 10% by weight with respect to the thermoformable base film and wherein the melt index of the thermoformable base film is between 1.7 and 2.3 g/10 min (190° C., 2160 g).
9. A thermoformed base comprising:
the thermoformable base film according to claim 1 ,
at least one cavity, and
a flange surrounding each of the cavities.
10. A packaged product comprising:
the thermoformed base according to claim 9 ,
a lid packaging component, and
a product,
wherein the lid packaging component is hermetically sealed to the flange of the thermoformed base and the product is enclosed in the at least one cavity of the thermoformed base.
11. The packaged product according to claim 10 , wherein the lid packaging component comprises a heat-sealing layer and a layer comprising at least one of metal and paper.
12. The packaged product according to claim 10 , wherein the lid packaging component is peelably sealed to the flange of the thermoformed base.
13. The packaged product according to claim 10 , wherein the thermoformed base and the lid packaging component are recyclable in the same recycle process.
14. The packaged product according to claim 10 , wherein the at least one cavity of the thermoformed base may be depressed manually, and the product may be pushed through the lid packaging component for product dispensing.
15. A thermoformable base film comprising:
a first layer comprising a blend of a high-density polyethylene or a medium-density polyethylene and a polyethylene having a density less than 0.92 g/cm3,
a second layer comprising from 60% to 90%, by weight, of a high-density polyethylene and from 2.5 to 30%, by weight of a hydrocarbon resin, and
a third layer comprising at least one polyethylene and having an overall density between about 0.92 g/cm 3 and 0.97 g/cm 3 ,
wherein the second layer is located between the first layer and the third layer,
wherein the second layer has a thickness that is from 25% to 90% of the total thickness of the thermoformable base film.
16. The thermoformable base film according to claim 15 , wherein the third layer comprises a blend of a high-density polyethylene or a medium-density polyethylene and a polyethylene having a density less than 0.92 g/cm 3 .
17. The thermoformable base film according to claim 15 , wherein the overall density of the thermoformable base film is less than 1.0 g/cm 3 .
18. A thermoformable base film comprising:
a first layer comprising at least one polyethylene and having an overall density between about 0.92 g/cm 3 and 0.97 g/cm 3 ,
a second layer comprising from 60% to 90%, by weight, of a high-density polyethylene and from 2.5 to 30%, by weight of a hydrocarbon resin, and
a third layer comprising a blend of a high-density polyethylene or a medium-density polyethylene and a polyethylene having a density less than 0.92 g/cm 3 ,
wherein the second layer is located between the first layer and the third layer,
wherein after thermoforming, the thermoformable base film maintains a shape taken during thermoforming.
19. The thermoformable base film according to claim 18 , wherein the second layer has a thickness that is from 25% to 90% of the total thickness of the thermoformable base film.
20. The thermoformable base film according to claim 18 , further comprising a fourth layer comprising a high-density polyethylene and an inorganic particle, wherein the inorganic particle is present in the fourth layer at a level of at least 5% by weight and wherein the fourth layer is between the first layer and the third layer.