Support structure of inverted lamella for tall ROI
Lamellae with thin regions for TEM of regions of interest include oppositely situated S-shaped cut faces that define a waist region. In some examples, the waist has a thickness of less than 25 nm and defines a double tapered region of height of between 400 nm and 800 nm that is suitable for TEM. A portion of the lamella at the top surface can comprising a metallic or other coating than serves to support the lamella.
1 . A method of preparing a lamella, comprising:
directing an ion beam to a back surface of a specimen at a first angle and at a first dose to form a first cut face having an S-shape; and
directing the ion beam to the back surf ace of the specimen at a second angle and at a second dose to form a second cut face having a second S-shape, wherein the first dose and the second dose are selected to produce a lamella having a waist.
2 . The method of claim 1 , wherein the waist is situated proximate a front surface or a back surface of the specimen.
3 . The method of claim 1 , wherein the first angle is opposite the second angle.
4 . The method of claim 1 , wherein the first S-shape is an opposite the second S-shape with respect to an axis perpendicular to the back surface or a front surface of the specimen.
5 . The method of claim 1 , wherein the ion beam is scanned along the back surface of the specimen to form the first cut face and the second cut face and to thin the waist.
6 . The method of claim 1 , wherein the first angle and second angle have magnitudes of less than 10 degrees, 7.5 degrees, 6 degrees, 5 degrees, 5, degrees, 2.5 degrees, 2 degrees, or 1 degree with respect to an axis perpendicular to the back surface and the first angle is opposite the second angle.
7 . The method of claim 1 , wherein the specimen includes a silicon substrate, a device layer, and a coating layer at a front surface opposite the back surface, and the waist is situated within the device layer.
8 . The method of claim 7 , wherein the device layer has a thickness between 200 nm and 800 nm, the coating layer has a thickness between 200 nm and 800 nm, the waist dimension is between 10 nm and 40 nm, and the waist is situated between 200 nm and 800 nm from the front surface.
9 . The method of claim 1 , comprising rotating the specimen to a first rotation angle and second rotation angle so that the ion beam is directed to the back surface of the specimen at the first angle and the second angle, respectively.
10 . The method of claim 1 , further comprising:
directing the ion beam to the back surface of a specimen at the first angle and the second angle at a first beam energy followed by a second beam energy that is lower than the first beam energy; and
exposing the lamella to the ion beam to thin the lamella.
11 . A lamella, comprising:
a specimen section defined by tapered cut faces that extend from a surface corresponding to a specimen back surface to a waist and from a specimen surface corresponding to a specimen front surface to the waist, wherein the tapered cut faces are S-curved cut faces have oppositely curved S-shapes.
12 . The lamella of claim 11 , wherein the waist is situated proximate the front surface.
13 . The lamella of claim 11 , wherein the specimen section at the front surface includes a portion of a metallic coating layer.
14 . The lamella of claim 13 , wherein the specimen section associated with the waist includes a portion of a device layer.
15 . The lamella of claim 13 , wherein the lamella has a height of between 2 μm and 10 μm, 5 μm and 10 μm, or 6 μm to 9 μm, a waist thickness is less than 10 nm, 20 nm, 50 nm, 40 nm, 50 nm, or 100 nm, a distance from the specimen surface corresponding to the front surface of the specimen section to the waist is greater than 100 nm, 200 nm, 500 nm, 400 nm, or 500 nm, and a depth of the specimen section is between 1 μm and 10 μm.
16 . A lamella, comprising:
a specimen section defined by tapered cut faces that extend from a surface corresponding to a specimen back surface to a waist and from a specimen surface corresponding to a specimen front surface to the waist, wherein the lamella has a height of between 2 μm and 10 μm, 5 μm and 10 μm, or 6 μm to 9 μm, a waist thickness is less than 10 nm, 20 nm, 50 nm, 40 nm, 50 nm, or 100 nm, a distance from the specimen surface corresponding to the front surface of the specimen section to the waist is greater than 100 nm, 200 nm, 500 nm, 400 nm, or 500 nm, and a depth of the specimen section is between 1 μm and 10 μm.
17 . The lamella of claim 16 , wherein the waist is situated proximate the front surface.
18 . The lamella of claim 16 , wherein the specimen section at the front surface includes a portion of a metallic coating layer.
19 . The lamella of claim 16 , wherein the specimen section associated with the waist includes a portion of a device layer.