Article comprising a rubber-like film-based article firmly fixed to a substrate
An article includes a substrate, and a film-based article comprising a non-crosslinked thermoplastic rubber. At least a portion of the film-based article is fixed to the substrate. In particular, said portion of the film-based article is firmly fixed to the substrate by heat sealing at a temperature of 190 to 250° C. for at least 1 second, without using a glue, an adhesive coating, or a corona discharge treatment.
1 . An article comprising:
a substrate, wherein the substrate is made of a material selected from the group consisting of non-crosslinked thermoplastic rubbers, polyamides, polyesters, thermoplastic polyurethanes and combinations thereof; and
a film-based article consisting essentially of a non-crosslinked thermoplastic rubber,
wherein at least a portion of the film-based article is in contact with the substrate to form a contact area, and at least a portion of the contact area is heat-sealed without using a glue, an adhesive coating, or a corona discharge treatment;
wherein the heat-sealed contact area between the film-based article and the substrate has a seal strength of at least 5 N/25 mm; and
wherein the non-crosslinked thermoplastic rubber is a thermoplastic styrenic block copolymer, which is selected from the group consisting of styrene-isoprene-styrene block copolymers (SIS), styrene-isobutylene-styrene block copolymers (SIBS), styrene-butadiene-styrene block copolymers (SBS), styrene-ethylene-butylene-styrene block copolymers (SEBS), styrene-ethylene-propylene-styrene block copolymers (SEPS), styrene-ethylene-ethylene-propylene-styrene block copolymers (SEEPS), and any combinations thereof.
2 . The article according to claim 1 , wherein the non-crosslinked thermoplastic rubber is a block copolymer of the general formula (I):
A-B-Y-(B-A) n (I),
wherein
each A is independently a polymer block composed of at least 90 mol % of an alkenyl aromatic hydrocarbon,
the content of A by weight of the total weight of the polymer is in the range of 9 to 12%,
Y is the remnant of a coupling agent having a functionality greater than 2,
the degree of branching is n+1, wherein n is an integer from 2 to 4,
each B is independently an olefinically unsaturated polymer block composed of at least 90 mol % of one or more conjugated dienes,
the block copolymer has a coupling efficiency in the range of 84 to 100%,
each A block independently has a weight average molecular weight ranging from 10,000 to 12,000 g/mol, and
each B block independently has a weight average molecular weight ranging from 80,000 to 120,000 g/mol, wherein the molecular weights are determined pursuant to ASTM 3536 using mono-dispersed polystyrene standards.
3 . The article according to claim 2 , wherein in the formula (I) each B is a polymer block composed of at least 90 mol % of isoprene and each A is a polymer block composed of at least 90 mol % of styrene.
4 . The article according to claim 1 , wherein the film-based article has a thickness of 1 μm to 10 μm.
5 . The article according to claim 1 , wherein the film-based article has been prepared by coagulation dipping using a latex of the non-crosslinked thermoplastic rubber, wherein the coagulation dipping comprises:
i) dipping a mold into a coagulant solution;
ii) removing the mold from the coagulant solution and drying the mold;
iii) dipping the dried mold into a latex of the non-crosslinked thermoplastic rubber so as to form the film-based article comprising the non-crosslinked thermoplastic rubber on the mold;
iv) removing the mold from the latex and pre-curing the latex with the film-based article;
v) curing the film-based article; and
vi) removing the film-based article from the mold.
6 . The article according to claim 5 , wherein the coagulation dipping further comprises leaching the film-based article in water between the steps iv) and v).
7 . The article according to claim 1 , wherein the substrate is a fabric.
8 . The article according to claim 1 , wherein the contact area is heat sealed for at least 10 seconds.
9 . The article according to claim 1 , wherein a seal strength between the film-based article and the substrate is at least 15 N/25 mm.
10 . The article according to claim 1 , wherein the film-based article has a tensile strength of at least 19 MPa, a 10% Young's modulus of less than 0.25 MPa, and a complex modulus at 120° C. of at least 5.6×10 5 Pa.
11 . The article according to claim 1 , wherein
i) the film-based article has a form of a surgical glove and the substrate is a surgical coat or an arm portion of a surgical coat, or
ii) both the film-based article and the substrate are rubber-like film-based articles, wherein each of the substrate and the film-based article is selected from the group consisting of gloves, customized clothes, articles of pleasure industry, shoe soles, and any combinations thereof, or
iii) the film-based article has a form of a catheter balloon and the substrate is a catheter tube made of a thermoplastic polymer, or
iv) the substrate is a breathable film for wound dressing, a sleeve for rubber gloves or a rubber-like seal for protective suits.