RAPID SOLID-STATE FOAMING
Disclosed, among other things, are ways to manufacture reduced density thermoplastics using rapid solid-state foaming and machines useful for the saturation of plastic. In one embodiment, a foaming process may involve saturating a semi-crystalline polymer such as Polylactic Acid (PLA) with high levels of gas, and then heating, which may produce a reduced density plastic having high levels of crystallinity. In another embodiment, a foaming process may produce layered structures in reduced density plastics with or without integral skins. In another embodiment, a foaming process may produce deep draw structures in reduced density plastics with or without integral skins. In yet another embodiment, a foaming process may utilize additives, blends, or fillers, for example. In yet another embodiment, a foaming process may involve saturating a semi-crystalline polymer such as Polylactic Acid (PLA) with high levels of gas, and then heating, which may produce a reduced density plastic having high levels of crystallinity.
1 .- 35 . (canceled)
36 . An article, comprising:
a non-laminated polymer sheet including at least 60% by weight of a polylactic acid polymer material, the non-laminated polymer sheet having a first outer region, a second outer region, and an inner region disposed between the first outer region and the second outer region,
the first outer region and the second outer region including cells having a first average dimension, and
the inner region including elongated cells having a second average dimension, the second average dimension greater than the first dimension, wherein the elongated cells have a length to width aspect ratio of at least 3:1, and
wherein the cells in the first outer region, the second outer region, and the inner region are formed by heating the non-laminated polymer sheet after the non-laminated polymer sheet has been exposed to a gas at a pressure of at least 500 PSI for a predetermined time period less than 15 minutes, the predetermined time period sufficient to at least partially saturate the non-laminated polymer sheet with the gas.
37 . The article of claim 36 , wherein the non-laminated polymer sheet withstands deformation when at least one of the first outer region and the second outer region are exposed to a temperature of at least 180° F.
38 . The article of claim 36 , wherein the first average dimension is 50 micrometers or less.
39 . The article of claim 36 , wherein the second average dimension is at least 51 micrometers.
40 . The article of claim 36 , wherein the first outer region and the second outer region have a higher level of crystallinity than the inner region.
41 . The article of claim 36 , further comprising:
an additive.
42 . The article of claim 41 , wherein the additive is a crystallizing additive.
43 . The article of claim 41 , wherein the additive is selected from the group consisting of polybutyl succinate, polycaprolactone and polyhydroxyalkanoate.
44 . The article of claim 36 , wherein the non-laminated polymer sheet includes filler.
45 . The article of claim 36 , further comprising:
a skin disposed on at least one of the first outer region and the second outer region.
46 . The article of claim 36 , further comprising:
a coating disposed on at least one of the first outer region and the second outer region.
47 . An article, comprising:
a non-laminated polymer sheet including at least 60% by weight of a polylactic acid polymer material, the non-laminated polymer sheet having a first outer region, a second outer region, and an inner region disposed between the first outer region and the second outer region,
the first outer region and the second outer region including a first plurality of cells having a first average dimension, and
the inner region including a second plurality of cells having a second average dimension, the second average dimension being greater than the first average dimension,
wherein the cells in the first outer region, the second outer region, and the inner region are formed by heating the non-laminated polymer sheet after the non-laminated polymer sheet has been exposed to a gas at a pressure of at least 500 PSI for a predetermined time period less than 15 minutes, the predetermined time period sufficient to at least partially saturate the non-laminated polymer sheet with the gas, and
wherein the article is in the form of a foam film or panel having a relative density of 5 to 70% of solid PLA.
48 . The article of claim 47 , wherein the first average dimension is 50 micrometers or less.
49 . The article of claim 47 , wherein second average dimension is at least 51 micrometers.
50 . The article of claim 47 , wherein the non-laminated polymer sheet withstands deformation when at least one of the first outer region and the second outer region are exposed to a temperature of at least 180° F.
51 . The article of claim 47 , wherein the predetermined time period is less than 10 minutes.
52 . An article, comprising:
a non-laminated polymer sheet including polylactic acid polymer and a biodegradable polymer filler, the non-laminated polymer sheet having a first outer region, a second outer region, and an inner region disposed between the first outer region and the second outer region,
the first outer region and the second outer region including a first plurality of cells having a first average dimension, and
the inner region including a second plurality of cells having a second average dimension, the second average dimension being greater than the first average dimension,
wherein the cells in the first outer region, the second outer region, and the inner region are formed by heating the non-laminated polymer sheet after the non-laminated polymer sheet has been exposed to a gas at a pressure of at least 500 PSI for a predetermined time period less than 15 minutes, the predetermined time period sufficient to at least partially saturate the non-laminated polymer sheet with the gas.
53 . The article of claim 52 , wherein the first average dimension is 50 micrometers or less.
54 . The article of claim 52 , wherein the second average dimension is at least 51 micrometers.
55 . The article of claim 52 , wherein the predetermined time period is less than 10 minutes.