Extended release asphaltene inhibitor composition
A nanoparticle for well-treatment applications and compositions and methods of making and using the same can include a carrier material and an asphaltene inhibitor. The asphaltene inhibitor is capable of being released from the carrier material. The nanoparticle can have a size of 10 nanometers (nm) to 500 nm.
1. A nanoparticle comprising a carrier material and an asphaltene inhibitor, wherein the asphaltene inhibitor is releasable from the carrier material,
wherein the nanoparticle has a core-shell structure comprising the asphaltene inhibitor and a porous shell comprising the carrier material,
wherein the nanoparticle has a diameter of 250 nm to 350 nm, the thickness of the shell is 50 nm to 150 nm, and at least 90 wt. % of the core, based on the total weight of the core, comprises the asphaltene inhibitor, and
wherein the shell comprises the asphaltene inhibitor on at least a portion of the shell surface and in the pores of the shell.
2. The nanoparticle of claim 1 , having a size of 50 nm to 400 nm.
3. The nanoparticle of claim 2 , wherein the nanoparticle comprises 20 wt. % to 80 wt. %, of the asphaltene inhibitor.
4. The nanoparticle of claim 1 , wherein the asphaltene inhibitor is physically entrapped within the carrier material and/or bound to the carrier material through an ionic bond, a covalent bond, a hydrogen bond, a van der Waals interaction or by adsorption onto a surface of the carrier material.
5. The nanoparticle of claim 4 , wherein the asphaltene inhibitor is adsorbed onto the surface of the carrier material.
6. The nanoparticle of claim 1 , wherein at least a portion of the surface of the nanoparticle comprises a surface modifying agent.
7. The nanoparticle of claim 1 , wherein the carrier material is a silica matrix.
8. The nanoparticle of claim 7 , wherein the silica matrix is an open-celled porous silica matrix having an average pore size of 2 nm to 50 nm.
9. The nanoparticle of claim 8 , wherein at least a portion of the asphaltene inhibitor is comprised in the pores of the porous silica matrix.
10. The nanoparticle of claim 1 , wherein the carrier material is a silica matrix, and a surface modifying agent is 3-aminopropyltriethoxysilane, and the nanoparticle further comprises a cationic surfactant comprising cetyltrimethylammonium bromide (CTAB).
11. The nanoparticle of claim 1 , wherein the carrier material is a polymer matrix.
12. The nanoparticle of claim 11 , wherein the polymer matrix comprises a polyolefin.
13. The nanoparticle of claim 12 , wherein the polyolefin is a polyethylene.
14. The nanoparticle of claim 13 , wherein the polymer matrix has a melting point of 50° C. to 200° C.
15. The nanoparticle of claim 1 , wherein the asphaltene inhibitor is capable of being released from the nanoparticle over an extended period of time.
16. A well treatment composition comprising a plurality of the nanoparticles of claim 1 .
17. The well treatment composition of claim 16 , wherein the well-treatment composition comprises 2000 kg to 50000 kg of the nanoparticles, and is capable of treating subterranean formations and/or wells for 300000 barrels to 8000000 barrels of oil produced.
18. The well treatment composition of claim 16 , further comprising water, a surfactant, or an organic solvent, or any combinations thereof.
19. A method of treating a subterranean formation or a wellbore, the method comprising injecting the composition of claim 16 into the wellbore, the wellbore intersecting the subterranean formation.