POLYAMIDE COMPOSITION
The present invention relates to a polyamide composition comprising a polyamide which is the poly condensation product of an acid component and an amine component, the acid component comprising, per mole of acid component; −30 to 50 mol. % of fatty acid dimer(s); −30 to 50 mol. % of aliphatic dibasic acid(s); −0 to 10 mol. % of chain limiter(s); the amine component comprising, per mole of amine component; −10 to 40 mol. % of cycloaliphatic diamine(s); and −50 to 80 mol. % of aliphatic diamine(s) comprising 3 to 12 carbon atoms); −0 to 15 mol. % of polyetheramine(s); said polyamide composition having; —a viscosity less than or equal to 4 Pa·s at 185° C.; and —a softening temperature ranging from 150° C. to 170° C.
1 - 20 . (canceled)
21 . Polyamide composition comprising a polyamide which is the product of polycondensation of an acid component and of an amine component,
the acid component comprising, per mole of acid component:
from 30 to 50 mol % of fatty acid dimer(s);
from 30 to 50 mol % of aliphatic diacid(s); and
from 0 to 10 mol % of chain limiter(s);
the amine component comprising, per mole of amine component:
from 10 to 40 mol % of cycloaliphatic diamine(s);
from 50 to 80 mol % of aliphatic diamine(s) comprising from 3 to 12 carbon atoms; and
from 0 to 15 mol % of polyetheramine(s);
said polyamide composition having:
a viscosity of less than or equal to 4 Pa·s at 185° C.; and
a softening point ranging from 150° C. to 170° C.
22 . Composition according to claim 21 , characterized in that it has a viscosity at 185° C. ranging from 0.5 to 4 Pa·s.
23 . Composition according to claim 21 , characterized in that it has a softening point ranging from 150° C. to 165° C.
24 . Composition according to claim 21 , characterized in that the fatty acid dimer is the reaction product of a coupling of unsaturated monocarboxylic acids.
25 . Composition according to claim 21 , characterized in that the aliphatic diacid is chosen from saturated aliphatic dicarboxylic acids.
26 . Composition according to claim 25 , characterized in that sebacic acid (C 10 ) or dodecanedioic acid (C 12 ) represents at least 75 mol % of the aliphatic dicarboxylic acids.
27 . Composition according to claim 21 , characterized in that the chain limiter is chosen from monocarboxylic acids which can comprise at least one heteroatom (O, S, Cl, F) or the corresponding esters, or monoisocyanates.
28 . Composition according to claim 21 , characterized in that the aliphatic diamine is chosen from saturated, linear or branched, aliphatic diamines comprising from 3 to 12 carbon atoms.
29 . Composition according to claim 21 , characterized in that the aliphatic diamine is hexanediamine.
30 . Composition according to claim 21 , characterized in that the cycloaliphatic diamine is chosen from bis(3,5-dialkyl-4-aminocyclohexyl) methane, bis(3,5-dialkyl-4-aminocyclohexyl) ethane, bis(3,5-dialkyl-4-aminocyclohexyl) propane, bis(3,5-dialkyl-4-aminocyclohexyl) butane, bis(3-methyl-4-aminocyclohexyl) methane (BMACM or MACM), bis(p-aminocyclohexyl) methane (PACM), isopropylidenedi(cyclohexylamine) (PACP), isophoronediamine, piperazine, aminoethylpiperazine, dimethylpiperazine, 4,4′-trimethylenedipiperidine, 1,4-cyclohexanediamine, a cycloaliphatic diamine having a carbon-based backbone (for example norbornylmethane, cyclohexylmethane, dicyclohexylpropane, di(methylcyclohexyl), di(methylcyclohexyl) propane) and their mixtures.
31 . Composition according to claim 21 , characterized in that the amine component does not comprise ethylenediamine (EDA).
32 . Composition according to claim 21 , characterized in that the amine component comprises, per mole of amine component, from 2 to 15 mol %.
33 . Composition according to claim 21 , characterized in that the polyamide is the product of polycondensation of an acid component and of an amine component,
the acid component comprising, per mole of acid component:
from 42 to 49 mol % of fatty acid dimer(s);
from 39 to 50 mol % of aliphatic diacid(s); and
from 3 to 10 mol % of chain limiter(s);
the amine component comprising, per mole of amine component:
from 25 to 40 mol % of cycloaliphatic diamine(s);
from 55 to 75 mol % of aliphatic diamine(s) comprising from 3 to 12 carbon atoms; and
from 5 to 15 mol % of polyetheramine(s).
34 . Composition according to claim 21 , characterized in that it comprises more than 90% by weight of polyamide as defined according to claim 21 , with respect to the total weight of said polyamide composition.
35 . Composition according to claim 21 , characterized in that it has a glass transition temperature Tg ranging from 0° C. to −67° C.
36 . Composition according to claim 21 , characterized in that it results in a tensile strength of greater than or equal to 3 MPa.
37 . Composition according to claim 21 , characterized in that it exhibits an elongation at break of greater than or equal to 80%.
38 . Composition according to claim 21 , characterized in that it is a hot-melt adhesive composition.
39 . Moulded article comprising an insert and the polyamide composition according to claim 21 , said insert being overmoulded at least in part by the polyamide composition.
40 . A hot-melt adhesive for the low-pressure overmoulding of a heat-sensitive battery comprising the polyamide composition according to claim 21 .