SUPERABSORBENT MATERIALS AND METHODS OF MAKING THE SAME
Provided are superabsorbent materials composed of agar, and one or more water-soluble natural polysaccharides, and dietary compositions containing such superabsorbent materials. The disclosed superabsorbent materials have various food and therapeutic applications and can be used as loading vehicles for nutrients and therapeutic agents. Also provided are methods for preparing such superabsorbent materials.
1 . A superabsorbent material having a porous network structure without any chemical cross-linking, comprising agar and one or more water-soluble natural polysaccharides; wherein the superabsorbent material is prepared by the steps consisting of:
adding the agar and the one or more water-soluble natural polysaccharide to water to form a mixture;
heating the mixture to a temperature of between 80° C. and 100° C. until the one or more polysaccharides are completely dissolved;
allowing the mixture to cool to form a gel;
freezing the gel to induce cryogelation;
drying the gel to obtain the superabsorbent material; and
optionally pulverizing the superabsorbent material to obtain the superabsorbent material in a powder form.
2 . The superabsorbent material of claim 1 , wherein the one or more water-soluble natural polysaccharides are selected from the group consisting of konjac gum, carrageenan, locust bean gum, xanthan gum, tamarind seed gum, guar gum, alginate, pectin, gellan gum, chitosan, Arabic gum, a soluble starch, and a combination thereof.
3 . The superabsorbent material of claim 1 , wherein, upon rehydration at room temperature, the superabsorbent material expands in volume in less than 2 hours, less than 1.5 hours, less than 1 hour, less than 30 minutes, or less than 15 minutes; and maintains a well-defined shape for at least 24 hours, at least 36 hours, or at least 48 hours under a neutral pH condition or a human gastric pH condition.
4 . The superabsorbent material of claim 1 , wherein the superabsorbent material has an absorption ratio of at least 10 times or up to 200 times of its own weight in deionized water, or at least 5 times or up to 100 times of its own weight in an artificial gastric juice.
5 . The superabsorbent material of claim 1 , wherein the superabsorbent material has a volume expansion ratio of at least 5 times or up to 150 times in deionized water, or at least 5 times to up to 100 times in an artificial gastric juice.
6 . The superabsorbent material of claim 1 , wherein the one or more water-soluble natural polysaccharides comprise konjac gum and carrageenan.
7 . The superabsorbent material of claim 1 , wherein the superabsorbent material comprises at least 10% by weight of agar.
8 . The superabsorbent material of claim 1 , wherein the superabsorbent material comprises at least 20% by weight of carrageenan.
9 . The superabsorbent material of claim 1 , wherein the superabsorbent material comprises agar, carrageenan, and konjac gum at a ratio of 10:1:1, 1:1:1, 1:1:2, 1:2:1, 2:1:1, 2:5:5, or 3:1:1.
10 . The superabsorbent material of claim 1 , wherein the superabsorbent material comprises agar, carrageenan, and konjac gum at a weight ratio of 1:1:1, 1:1:2, or 1:2:1.
11 . The superabsorbent material of claim 1 , wherein the drying step comprises directly freeze-drying the gel in a frozen state.
12 . The superabsorbent material of claim 1 , wherein the drying step comprises thawing the gel in a frozen state to form a thawed gel and drying the thawed gel at a temperature of between 50° C. and 60° C.
13 . The superabsorbent material of claim 1 , wherein the drying step comprises:
thawing the gel in a frozen state to form a thawed gel;
filtering the thawed gel to obtain a filter cake; and
drying the filter cake.
14 . A superabsorbent material having a porous structure without any chemical cross-linking, comprising agar, carrageenan, and konjac gum.
15 . The superabsorbent material of claim 14 , wherein the superabsorbent material comprises at least 10% by weight of agar.
16 . The superabsorbent material of claim 14 , wherein the superabsorbent material comprises at least 20% by weight of carrageenan.
17 . The superabsorbent material of claim 14 , wherein the superabsorbent material comprises agar, κ-carrageenan, and konjac gum at a ratio of 10:1:1, 1:1:1, 1:1:2, 1:2:1, 2:1:1, 2:5:5, or 3:1:1.
18 . The superabsorbent material of claim 14 , wherein the superabsorbent material comprises agar, κ-carrageenan, and konjac gum at a ratio of 1:1:1, 1:1:2, or 1:2:1.
19 . The superabsorbent material of claim 14 , wherein, upon rehydration, the superabsorbent material expands in volume in less than 2 hours, less than 1.5 hours, less than 1 hour, less than 30 minutes, or less than 15 minutes; and maintains a well-defined shape for at least 24 hours, at least 36 hours, or at least 48 hours under a neutral pH condition or a human gastric pH condition, and at room temperature or at human body temperature.
20 . The superabsorbent material of claim 14 , wherein the superabsorbent material has a volume expansion ratio of at least 5 times or up to 150 times in deionized water, or at least 5 times to up to 100 times in an artificial gastric juice.
21 . The superabsorbent material of claim 14 , wherein the superabsorbent material has a volume expansion ratio of at least 5 times or up to 150 times in deionized water, or at least 5 times to up to 100 times in an artificial gastric juice.