Sulfonation method for efficient scaleup synthesis of Janus carbon nanofluids from waste plastics
A method of preparing an enhanced oil recovery composition is described. The method includes carbonizing a waste plastic material to provide carbon microparticles, functionalizing the carbon microparticles with a SO 3 -containing gas such that the carbon microparticles have a hydrophilic surface, and grinding the carbon microparticles to provide carbon nanoparticles. The carbon nanoparticles have a hydrophilic surface and a hydrophobic surface. A method of enhanced oil recovery is also described.
1 . A method of preparing an enhanced oil recovery composition comprising:
carbonizing a waste plastic material to provide carbon microparticles;
functionalizing the carbon microparticles with an SO 3 -containing gas such that the carbon microparticles comprise a hydrophilic surface, wherein functionalizing the carbon microparticles with the SO 3 -containing gas comprises heating the carbon microparticles at a temperature from about 30 to 70° C. at a flow rate from 0.1 milliliter per minute (mL/min) to 1 ml/min; and
grinding the carbon microparticles to provide carbon nanoparticles, wherein the carbon nanoparticles comprise a hydrophilic surface and a hydrophobic surface.
2 . The method of claim 1 , wherein carbonizing a waste plastic material further comprises grinding to provide carbon microparticles.
3 . The method of claim 1 , further comprising mixing the carbon nanoparticles with an aqueous-based fluid to provide an enhanced oil recovery fluid.
4 . The method of claim 1 , wherein the waste plastic material comprises a polymer selected from the group consisting of polypropylene (PP), polystyrene (PS), acrylonitrile butadiene styrene (ABS), polyethylene terephthalate (PET), polyester (PES), polyamide (PA), polyvinyl chloride (PVC), polyurethane (PU), polycarbonate (PC), polyvinylidene chloride (PVDC), polyethylene (PE), and combinations thereof.
5 . The method of claim 1 , wherein the waste plastic material is a plastic waste bottle.
6 . The method of claim 1 , wherein carbonizing the waste plastic material comprises heating the waste plastic material at a temperature of a range of 300 to 550° C.
7 . The method of claim 1 , wherein the carbon microparticles have an average particle size ranging 5 to 20 μm.
8 . The method of claim 1 , wherein functionalizing the carbon microparticles with the SO 3 -containing gas comprises heating the carbon microparticles at a temperature of 50° C. at a flow rate of 0.1 mL/min.
9 . The method of claim 8 , wherein functionalizing the carbon microparticles with the SO 3 -containing gas further comprises heating for 15 minutes.
10 . The method of claim 1 , wherein the hydrophilic surface functionality is a sulfonate.
11 . The method of claim 1 , wherein grinding the carbon microparticles comprises ball milling the carbon microparticles for an amount of time from 0.5 to 8 hours with a speed of 2000 to 4000 rpm.
12 . The method of claim 1 , wherein the carbon nanoparticles have an average particle size ranging from 5 to 500 nm.
13 . The method of claim 1 , wherein the hydrophobic surface is a non-sulfonated carbon surface.
14 . The method of claim 11 , wherein the hydrophobic surface is generated by ball milling.
15 . The method of claim 3 , wherein the aqueous-based fluid is water, seawater, or brine.
16 . The method of claim 3 , wherein the aqueous-based fluid comprises one or more additives selected from the group consisting of surfactant, stabilizers, and combinations thereof.