Modified lithium ion negative electrode material, and preparation therefor and use thereof
The present disclosure relates to the technical field of batteries, and in particular, to a modified lithium ion negative electrode material, and preparation therefor and use thereof. The preparation method includes the following steps: dropwise adding a mixed solution of a titanium source and a lithium source into a mixed solution of an iron salt and an organic acid, adjusting the pH to 5.0-7.0, and stirring to obtain a wet gel; drying and crushing the wet gel, and then calcinating to obtain a LiFeTiO 4 composite oxide; and reducing the LiFeTiO 4 composite oxide to obtain the modified lithium ion negative electrode material. In the present disclosure, a spinel modified negative electrode material lithium iron titanium oxide is synthesized by using a citric acid sol-gel method, thereby not only greatly improving the charging and discharging capacity thereof, but also improving the large-current charging and discharging capability thereof.
1. A preparation method for a modified lithium ion negative electrode material, comprising the following steps,
S1: adding an organic acid to an iron salt solution to obtain a solution I;
at the same time, dissolving a titanium source and a lithium source in an alcohol solvent to obtain a solution II;
S2: dropwise adding the solution II into the solution I, adjusting the pH to 5.0-7.0, and continuing stirring to obtain a wet gel;
S3: drying the wet gel to form a xerogel, grinding and crushing the xerogel, and calcinating to obtain a LiFeTiO 4 composite oxide; and
S4: under the action of a reducing gas, performing a heat treatment on the LiFeTiO 4 composite oxide to obtain the modified lithium ion negative electrode material, wherein the chemical formula of the modified lithium ion negative electrode material is LiFeTiO x , where 1<x<4;
in step S3, the calcination is carried out twice, in which the temperature for the first calcination is 260-350° C., and the time is 1-5 h; and the temperature for the second calcination is 550-750° C., and the time is 1.5-4 h;
in step S4, the reducing gas is hydrogen, the temperature for the heat treatment is 350-650° C., and the time is 2-8 h.
2. The preparation method for a modified lithium ion negative electrode material according to claim 1 , wherein the molar ratio of the iron salt in the solution I to the lithium source in the solution II is (0.1-0.3): 1 .
3. The preparation method for a modified lithium ion negative electrode material according to claim 1 , wherein in step S1, the addition amount of the organic acid is 1-5 times of the mole number of metal ions, and the metal ions are lithium ions, iron ions and titanium ions.
4. The preparation method for a modified lithium ion negative electrode material according to claim 1 , wherein
the iron salt is selected from one or more of ferric nitrate, ferric chloride and ferric sulfate;
the organic acid is selected from one or more of citric acid, malic acid and tartaric acid;
the titanium source is selected from one or more of tetrabutyl titanate, n-butyl titanate and isopropyl titanate;
the lithium source is selected from one or more of lithium acetate, lithium carbonate, lithium oxalate and lithium nitrate;
and the alcohol solvent is selected from one or more of ethanol, methanol, ethylene glycol and diethylene glycol.
5. The preparation method for a modified lithium ion negative electrode material according to claim 1 , wherein in step S2, the stirring is continued for 3-6 h under a condition of 30-50° C., so as to obtain a wet gel.
6. A modified lithium ion negative electrode material prepared by using the preparation method according to claim 1 .
7. A negative electrode sheet, comprising a negative electrode active material layer, wherein the negative electrode active material layer comprises the modified lithium ion negative electrode material according to claim 6 .
8. A battery, comprising the negative electrode sheet according to claim 7 .