Composite release films, and devices and methods using composite release film in field of additive manufacturing
A composite release film may be configured to separate a current cured layer from a photocuring surface during a photocuring three-dimensional (3D) printing process. The composite release film may include a plastic layer and an elastic layer. An upper surface of the plastic layer may be the photocuring surface, and a lower surface of the plastic layer may fit with an upper surface of the elastic layer. The elastic layer may include an elastic medium of the elastic layer and a reinforcing scaffold. The elastic medium of the elastic layer may be filled in pores of the reinforcing scaffold. The reinforcing scaffold in the elastic layer may include a plurality of protrusions on a lower surface of the elastic layer. In addition, a device and a method using the composite release film to prepare a 3D object through a photocuring 3D printing technique in the field of additive manufacturing are disclosed.
1 . A composite release film, configured to separate a current cured layer from a photocuring surface during a photocuring three-dimensional (3D) printing process, wherein the composite release film includes a plastic layer and an elastic layer, an upper surface of the plastic layer being the photocuring surface, and a lower surface of the plastic layer fitting with an upper surface of the elastic layer; an elastic modulus of a material of the plastic layer being larger than an elastic modulus of a material of the elastic layer material; and
a ratio of a difference between the elastic modulus of the material of the plastic layer and the elastic modulus of the material of the elastic layer to the elastic modulus of the material of the elastic layer being not larger than 20%.
2 . The composite release film of claim 1 , wherein the elastic layer includes an elastic medium of the elastic layer and a reinforcing scaffold, the elastic medium of the elastic layer being filled in pores of the reinforcing scaffold.
3 . The composite release film of claim 2 , wherein the reinforcing scaffold in the elastic layer includes a plurality of protrusions on a lower surface of the elastic layer.
4 . The composite release film of claim 1 , wherein a resistance to swelling of a material of the plastic layer is better than a resistance to swelling of a material of the elastic layer.
5 . The composite release film of claim 2 , wherein an elastic modulus of a material of the reinforcing scaffold in the elastic layer is larger than an elastic modulus of a material of the elastic medium of the elastic layer.
6 . The composite release film of claim 5 , wherein a ratio of a difference between the elastic modulus of the material of the reinforcing scaffold in the elastic layer and the elastic modulus of the material of the elastic medium of the elastic layer to the elastic modulus of the material of the elastic medium of the elastic layer is not larger than 20%.
7 . The composite release film of claim 1 , wherein a thickness of the plastic layer is less than a thickness of the elastic layer.
8 . The composite release film of claim 1 , wherein a material of the plastic layer includes polytetrafluoroethylene (PTFE) or fluorinated ethylene propylene (FEP).
9 . The composite release film of claim 2 , wherein a material of the elastic medium of the elastic layer includes polydimethylsiloxane (PDMS), polyurethane, or rubber.
10 . The composite release film of claim 2 , wherein a material of the reinforcing scaffold in the elastic layer includes porous PTFE or porous FEP.
11 . The composite release film of claim 3 , wherein an average height of the plurality of protrusions on the lower surface of the elastic layer is within a range of 100 nanometers to 20 microns.
12 . The composite release film of claim 1 , wherein the elastic modulus of the material of the plastic layer is within a range of 0.1 Mpa to 100 Mpa.
13 . The composite release film of claim 1 , wherein the elastic modulus of the material of the elastic layer is within a range of 0.1 Mpa to 100 Mpa.
14 . The composite release film of claim 2 , the material of the reinforcing scaffold in the elastic layer is the same as the material of the plastic layer.
15 . The composite release film of claim 1 , wherein a contact angle between photocurable liquid resin and the upper surface of the plastic layer is not less than 60 degrees.
16 . A device for photocuring three-dimensional (3D) printing, comprising:
a resin tank, configured to contain raw materials for printing including photocurable liquid resin, a bottom surface of the resin tank being transparent;
a composite release film placed on a bottom portion of the resin tank, configured to separate a current cured layer from a photocuring surface, the composite release film including a plastic layer and an elastic layer, wherein an upper surface of the plastic layer is the photocuring surface that is a contact surface with the liquid resin, a lower surface of the plastic layer fits with an upper surface of the elastic layer; an elastic modulus of a material of the plastic layer is larger than an elastic modulus of a material of the elastic layer material; and a ratio of a difference between the elastic modulus of the material of the plastic layer and the elastic modulus of the material of the elastic layer to the elastic modulus of the material of the elastic layer is not larger than 20%;
a build platform, a space between the build platform and the upper surface of the plastic layer of the composite release film being a printing region; and
a light source, configured to irradiate the liquid resin in the printing region to provide energy to form the current cured layer.
17 . The device for photocuring 3D printing of claim 16 , wherein the elastic layer includes an elastic medium of the elastic layer and a reinforcing scaffold, the elastic medium of the elastic layer being filled in pores of the reinforcing scaffold.
18 . The device for photocuring 3D printing of claim 17 , wherein the reinforcing scaffold in the elastic layer includes a plurality of protrusions on a lower surface of the elastic layer, the plurality of protrusions being in contact with the bottom surface of the resin tank.
19 . The device for photocuring 3D printing of claim 18 , wherein an average height of the plurality of protrusions on the lower surface of the elastic layer is within a range of 100 nanometers to 20 microns.
20 . The device for photocuring 3D printing of claim 16 , wherein a resistance to swelling of a material of the plastic layer is better than a resistance to swelling of a material of the elastic layer.