REVERSE OSMOSIS MEMBRANE AND METHOD OF PRODUCING THE SAME
A composite polyamide reverse osmosis membrane comprising a polyamide layer; where the polyamide layer has a thickness in the range of 50-250 nm, and large open spaces (i.e., free volumes); where the open spaces are defined by a ratio of water flux, J w , (gfd) divided by the average surface roughness, Ra, (nm) of the polyamide layer; wherein the composite polyamide reverse osmosis membrane has the ratio of J w /Ra>0.35 gfd/nm when tested at 65 psi, using an aqueous solution containing 250 ppm of NaCl; and a microporous support with a thickness ranging from 100-150 μm. The present invention also relates to processes of fabricating the composite polyamide reverse osmosis membrane.
1 . A composite polyamide reverse osmosis membrane comprising:
a polyamide layer; where the polyamide layer has a thickness in the range of 50-250 nm, and large open spaces (i.e., free volume); where the open spaces are defined by a ratio of water flux, J w , (gfd) divided by the average surface roughness, Ra, (nm) of the polyamide layer; wherein the composite polyamide reverse osmosis membrane has the ratio of J w /Ra>0.35 gfd/nm when tested at 65 psi, using an aqueous solution containing 250 ppm of NaCl.
2 . The composite polyamide reverse osmosis membrane of claim 1 , further comprising a microporous support;
wherein the microporous support comprises:
a polymeric layer with a thickness in the range of 30-80 μm; and
a fabric layer with a thickness in the range of 70-100 μm.
3 . The composite polyamide reverse osmosis membrane of claim 2 , wherein the polymeric layer is selected from the group consisting of a polysulfone polymer, a polyether sulfone polymer, a polyimide polymer, a polyamide polymer, a polypropylene polymer, a polyarylether sulfone polymer, and polyvinylidene fluoride polymers.
4 . The composite polyamide reverse osmosis membrane of claim 2 , wherein the fabric layer is a woven or non-woven support made from materials selected from the group consisting of polyethylene terephthalate (PET), polyester blends and polypropylene.