DURABLE, LOW LOADING OXYGEN EVOLUTION REACTION CATALYSTS AND METHODS OF FORMING SUCH CATALYSTS
The following disclosure relates to catalyst compositions for electrochemical cells and their methods of making. In one example, the method includes providing a supporting substrate and depositing an active catalyst composition onto a surface of the supporting substrate via atomic layer deposition (AID). A catalyst composition includes a conductive substrate and an active catalyst deposited on a surface of the conductive substrate via atomic layer deposition.
1 . A method of depositing an active catalyst composition on a substrate, the method comprising:
providing a supporting substrate comprising an electrospun fibrous nanowire, wherein the electrospun fibrous nanowire comprises tungsten doped titanium dioxide; and
depositing an active catalyst composition onto a surface of the supporting substrate via atomic layer deposition (ALD),
wherein the active catalyst composition comprises iridium oxide.
2 . The method of claim 1 , wherein the supporting substrate is a conductive substrate.
3 .- 5 . (canceled)
6 . The method of claim 2 , wherein the conductive substrate further comprises carbon nanotubes, silicon nanowires, nanofibers of conductive polymers, or combinations thereof.
7 . The method of claim 6 , wherein the conductive polymers comprise polyaniline, poly(3,4-ethylenedioxythiophene) (PEDOT), or a combination thereof.
8 .- 10 . (canceled)
11 . The method of claim 1 , wherein the active catalyst composition is deposited in islands comprising separate catalyst locations on the surface of the supporting substrate.
12 . The method of claim 11 , wherein a thickness of a layer of the active catalyst composition deposited on the surface of the supporting substrate is in a range of 0.1-100 nm.
13 . A catalyst composition comprising:
a conductive substrate comprising an electrospun fibrous nanowire, wherein the electrospun fibrous nanowire comprises tungsten doped titanium dioxide; and
an active catalyst deposited on a surface of the conductive substrate,
wherein the active catalyst comprises iridium oxide.
14 .- 16 . (canceled)
17 . The composition of claim 13 , wherein the conductive substrate further comprises carbon nanotubes, silicon nanowires, nanofibers of conductive polymers, or combinations thereof.
18 . The composition of claim 17 , wherein the conductive polymers comprise polyaniline, poly(3,4-ethylenedioxythiophene) (PEDOT), or a combination thereof.
19 .- 21 . (canceled)
22 . The composition of claim 13 , wherein the active catalyst is deposited in islands comprising separate catalyst locations on the surface of the conductive substrate.
23 . The composition of claim 13 , wherein a thickness of a layer of the active catalyst deposited on the surface of the conductive substrate is in a range of 0.1-100 nm.