Composite sheets and medical implants comprising such sheets
Disclosed herein are composite sheets and prosthetic medical devices formed therefrom. In an embodiment, a composite sheet has a thickness of 25-250 μm and comprises 10-70 mass %, based on the total mass of the composite sheet, of a knit fabric having thickness of 15-225 μm and comprising strands of 2-50 dtex, the strands comprising biocompatible polymer fibers, the strands comprising biocompatible polymer fibers, wherein the fabric comprises a thickness in a plurality of first locations, and pores in a plurality of second locations; and 30-90 mass %, based on the total mass of the composite sheet, of a polyurethane coating, wherein the polyurethane coating coats the fabric and fills the pores of the fabric such that the composite sheet is substantially impermeable to water.
1 . A composite sheet having a thickness of 25-250 μm and comprising:
(a) 10-70 mass %, based on the total mass of the composite sheet, of a knit fabric having thickness of 15-225 μm and comprising strands of 2-50 dtex, the strands comprising biocompatible polymer fibers, the strands comprising biocompatible polymer fibers, wherein the fabric comprises a thickness in a plurality of first locations, and pores in a plurality of second locations; and
(b) 30-90 mass %, based on the total mass of the composite sheet, of a polyurethane coating, wherein the polyurethane coating coats the fabric and fills the pores of the fabric such that the composite sheet is substantially impermeable to water; wherein
the composite sheet has a 1% secant modulus of from 1 to 100 MPa and a hardening transition point of from 5 to 75% in each of two orthogonal directions and the diagonal thereof.
2 . A composite sheet having a thickness of 25-250 μm and comprising:
(a) 10-70 mass %, based on the total mass of the composite sheet, of a knit fabric having thickness of 15-225 μm and comprising strands of 2-50 dtex, the strands comprising biocompatible polymer fibers, the strands comprising biocompatible polymer fibers, wherein the fabric comprises a thickness in a plurality of first locations, and pores in a plurality of second locations; and
(b) 30-90 mass %, based on the total mass of the composite sheet, of a polyurethane coating, wherein the polyurethane coating coats the fabric and fills the pores of the fabric such that the composite sheet is substantially impermeable to water; wherein
the composite sheet has a flexural rigidity per unit width of from 1 to 20 N·μm in each of two orthogonal directions and the diagonal thereof.
3 . The composite sheet according to claim 1 , wherein the composite sheet has a 1% secant modulus of from 1 to 100 MPa and a hardening transition point of from 5 to 75% in all directions.
4 . The composite sheet according to claim 1 , wherein the composite sheet has a flexural rigidity per unit width of from 1 to 20 N·μm in all directions.
5 . The composite sheet according to claim 1 , wherein the composite sheet has a flexural modulus of from 10 to 200 MPa in each of two orthogonal directions and the diagonal thereof.
6 . The composite sheet according to claim 1 , wherein the thickness in the plurality of first locations corresponds to the stacking of one or more strands at the plurality of first locations.
7 . The composite sheet according to claim 1 , wherein the composite sheet comprises a first side having a first roughness that corresponds to the differences in thickness of the composite sheet between the plurality of first locations and the plurality of second locations, and a second side having a second roughness, wherein the first roughness is greater than the second roughness.
8 . The composite sheet according to claim 1 , wherein the first locations correspond to the interconnection of a loop of one or more strands with the same or a different strand.
9 . The composite sheet according to claim 1 , wherein the knit fabric is a mesh having mesh openings of 25-250 μm.
10 . The composite sheet according to claim 1 , wherein the knit fabric is a warp knit.
11 . The composite sheet according to claim 1 , wherein the knit fabric is a raschel knit.
12 . The composite sheet according to claim 1 , wherein the knit fabric has a thickness of 15-125 μm and comprises strands of 2-15 dtex.
13 . The composite sheet according to claim 1 , wherein the composite sheet has a thickness of from 25 to 200 μm.
14 . The composite sheet according to claim 1 , wherein the fabric consists of strands comprising a UHMWPE yarn.
15 . The composite sheet according to claim 1 , wherein the polyurethane comprises a biocompatible and biostable polyurethane elastomer comprising polysiloxane segments and polycarbonate segments.
16 . A valve prosthesis comprising a leaflet comprising the composite sheet according to claim 1 .