Cubic boron nitride polycrystallite and method for producing the same
A cubic boron nitride (cBN) polycrystallite includes: a fine-grained cBN crystal of 10-60 nm in grain size; a coarse-grained cBN crystal of 100-250 nm in grain size; and a lamellar crystal consisting of stacked plate-like crystals of cBN with the maximum length perpendicular to the stacking direction not larger than 1000 nm and an aspect ratio smaller than 3, where the aspect ratio is defined as the maximum length divided by a maximum length in the stacking direction, and a mean grain size of the fine-grained, coarse-grained and lamellar crystals is not larger than 80 nm. This cBN polycrystallite can be obtained by performing, under 10 GPa or lower, heating a material made of hexagonal system boron nitride to a first temperature within 1300°-1600° C., maintaining it for a first predetermined period, heating it to a second temperature within 1700°-2100° C., maintaining it for a second predetermined period, and cooling it.
1. A cubic boron nitride polycrystallite, characterized in that:
the polycrystallite includes a mixture of:
a fine-grained crystal made of cubic boron nitride, with a grain size within a range from 10 to 60 nm;
a coarse-grained crystal made of cubic boron nitride, with a grain size within a range from 100 to 250 nm; and
a lamellar crystal consisting of a plurality of stacked plate-like crystals of cubic boron nitride, the lamellar crystal having a maximum length in a direction perpendicular to a stacking direction equal to or less than 1000 nm and an aspect ratio smaller than 3, where the aspect ratio is defined as the maximum length in the direction perpendicular to the stacking direction divided by a maximum length in the stacking direction;
an area ratio of the fine-grained crystal, the coarse grained crystal and the lamellar crystal in a transmission electron microscope image of the cubic boron nitride polycrystallite is within a range of (13-20):(60-75):(10-30); and
a mean grain size of the fine-grained crystal, the coarse-grained crystal and the lamellar crystal combined is equal to or smaller than 80 nm.
2. The cubic boron nitride polycrystallite according to claim 1 , characterized in that the mean grain size of the fine-grained crystal, the coarse-grained crystal and the lamellar crystal combined is equal to or smaller than 60 nm.
3. A method for producing a cubic boron nitride polycrystallite according to claim 1 , characterized by performing, under a pressure equal to or higher than 10 GPa, successive steps of heating a material made of hexagonal system boron nitride to a first temperature within a range from 1300° to 1600° C., maintaining the material at the first temperature for a first predetermined period of time, heating the material to a second temperature within a range from 1700° to 2100° C., maintaining the material at the second temperature for a second predetermined period of time, and cooling the material.
4. A method for producing a cubic boron nitride polycrystallite according to claim 2 , characterized by performing, under a pressure equal to or higher than 10 GPa, successive steps of heating a material made of hexagonal system boron nitride to a first temperature within a range from 1300° to 1600° C., maintaining the material at the first temperature for a first predetermined period of time, heating the material to a second temperature within a range from 1700° to 2100° C., maintaining the material at the second temperature for a second predetermined period of time, and cooling the material.
5. A cutting tool, comprising a cutting edge made of the cubic boron nitride polycrystallite according to claim 1 .
6. A cutting tool, comprising a cutting edge made of the cubic boron nitride polycrystallite according to claim 2 .
7. A grinding tool, comprising abrasive grains made of the cubic boron nitride polycrystallite according to claim 1 .
8. A grinding tool, comprising abrasive grains made of the cubic boron nitride polycrystallite according to claim 2 .
9. An indenter for hardness measurement, characterized by being made of the cubic boron nitride polycrystallite according to claim 1 .
10. An indenter for hardness measurement, characterized by being made of the cubic boron nitride polycrystallite according to claim 2 .