Direct lithium extraction compositions and methods
Sorbent compositions for direct lithium extraction (DLE). The sorbent compositions include a lithiated aluminum component and an inorganic binder, and are in the form of shaped particles. The lithiated aluminum component makes up about 50% w/w to about 90% w/w of the sorbent compositions, whereas the binder makes up about 10% w/w to about 50% w/w of the sorbent compositions. Processes for producing the sorbent compositions are also provided, as are methods of using the sorbent compositions for DLE.
1. A sorbent composition for direct lithium extraction (DLE), the sorbent comprising:
a lithiated aluminum component, the lithiated aluminum component selected from the group consisting of a lithiated aluminum trihydroxide (ATH), lithiated aluminum oxide and/or lithiated boehmite; and
an inorganic binder,
wherein the lithiated aluminum component makes up about 50% w/w to about 90% w/w of the sorbent composition, wherein the inorganic binder makes up about 10% w/w to about 50% w/w of the sorbent composition,
wherein the sorbent composition is in the form of shaped particles, the shaped particles having an average pore diameter of about 80 nm to about 230 nm.
2. The sorbent composition of claim 1 , wherein the lithiated aluminum component comprises lithiated ATH (LiDATH).
3. The sorbent composition of claim 1 , wherein the inorganic binder comprises a boehmite-based binder, a boehmite/silica-based binder, a colloidal silica binder, a waterglass binder, an aluminum phosphate binder, an aluminum halide-based binder and/or a combination thereof.
4. The sorbent composition of claim 1 , wherein the shaped particles have a particle size ranging from about 100 to about 4000 micron, optionally about 200 to about 1500 micron, optionally about 20 to about 100 micron or greater.
5. The sorbent composition of claim 1 , wherein the shaped particles have a diameter of about 0.5 mm to about 4.0 mm, optionally about 0.65 mm to about 1.75 mm, and a length to diameter ratio of about 0.25:1 to 5:1, optionally about 0.5:1 to 3.5:1.
6. The sorbent composition of claim 1 , wherein the sorbent composition comprises shaped particles having a Brunauer-Emmett-Teller (BET) surface area ranging from about 4 m 2 /g to about 105 m 2 /g, optionally about 4 m 2 /g to about 25 m 2 /g, optionally about 20 m 2 /g to about 45 m 2 /g, optionally about 45 m 2 /g to about 90 m 2 /g, optionally about 10 m 2 /g to about 105 m 2 /g, optionally about 50 m 2 /g to about 90 m 2 /g, optionally about 70 m 2 /g to about 105 m 2 /g.
7. The sorbent composition of claim 1 , wherein the sorbent composition comprises shaped particles having an average pore diameter of about 170 nm to about 230 nm.
8. The sorbent composition of claim 1 , wherein the shaped particles are spheronized, wherein the spheronized shaped particles are subsequently dried at about 120° C. or higher.
9. The sorbent composition of claim 1 , wherein the sorbent composition is heat treated, wherein the heat treatment comprises heating at about 120° C. to about 450° C.
10. The sorbent composition of claim 1 , wherein the sorbent composition is heat treated, wherein the heat treatment comprises heating for up to about 1 hour or greater.
11. The sorbent composition of claim 1 , wherein the shaped particles comprise dumbbell shaped particles, cylindrical shaped particles, spherical shaped particles, bilobe shaped particles, trilobe shaped particles, quadrilobed shaped particles and/or combinations thereof, wherein the shaped particles are shaped via extrusion, pelletizing, granulation, compaction, compaction/granulation, and/or pressing.
12. The sorbent composition of claim 1 , wherein the binder comprises sodium silicate, wherein the sodium silicate is at a concentration of about 10% w/w to about 50% w/w.
13. The sorbent composition of claim 1 , wherein the sorbent composition has a lithium adsorption capacity of about 3.0 mg/g (mg Li per g of sorbent) to about 7.5 mg/g.
14. The sorbent composition of claim 1 , wherein the sorbent composition comprises shaped particles having an average pore diameter of about 80 nm to about 170 nm.
15. The sorbent composition of claim 1 , wherein the sorbent composition comprises shaped particles having an average pore diameter of about 80 nm to about 115 nm.