DEVELOPER COMPOSITION FOR PHENOL-FREE DIRECT THERMAL RECORDING MEDIA
A recording medium comprises a substrate and a thermally responsive layer carried by the substrate. The thermally responsive layer includes a leuco dye and at least one developer. The recording medium is substantially phenol-free. The at least one developer comprises an N,N′-diphenylurea derivative selected from S-176 and TGMD.
1 . A recording medium, comprising:
a substrate; and
a thermally responsive layer carried by the substrate, the thermally responsive layer including a leuco dye and at least one developer;
wherein the recording medium is substantially phenol-free; and
wherein the at least one developer comprises an N,N′-diphenylurea derivative selected from S-176 and TGMD.
2 . The medium of claim 1 , wherein the developer comprises S-176.
3 . The medium of claim 1 , wherein the developer comprises TGMD.
4 . The medium of claim 1 , wherein the developer comprises S-176 and TGMD.
5 . The medium of claim 1 , wherein the substrate comprises a water-soluble paper or water-dispersible paper.
6 . The medium of claim 5 , comprising a base coat between the substrate and the thermally responsive layer.
7 . The medium of claim 6 , wherein the base coat includes a non-water-soluble binder.
8 . The medium of claim 4 , wherein the substrate comprises a water-soluble or water-dispersible paper.
9 . The medium of claim 1 , wherein a print quality of the recording medium when printed with a thermal printer energy setting of 11.7 mJ/mm 2 at a print speed of 6 inches per second (ips) is characterized by an ANSI value of at least 1.5.
10 . The medium of claim 9 , wherein the print quality of the printed recording medium is characterized by an ANSI value of at least 1.5 even where, before the thermal printing is performed, the recording medium is exposed to air at 40° C. and 90% relative humidity for 24 hours, then removed and cooled.
11 . The medium of claim 9 , wherein the print quality of the printed recording medium is still characterized by an ANSI value of at least 1.5 after the printed recording medium is exposed to air at 40° C. and 90% relative humidity for 24 hours, then removed and cooled.
12 . The medium of claim 1 , further comprising a top coat carried by the substrate such that the thermally responsive layer is disposed between the top coat and the substrate.
13 . The medium of claim 1 , wherein the thermally responsive layer has a coat weight of 2.5 to 7.5 g/m 2 .
14 . The medium of claim 1 , wherein the at least one developer comprises S-176 and a print quality of the recording medium when printed with a thermal printer energy setting of 11.7 mJ/mm 2 at a print speed of 6 inches per second (ips) is characterized by an ANSI value of at least 1.5.
15 . The medium of claim 14 , wherein the print quality of the printed recording medium is characterized by an ANSI value of at least 1.5 even where, before the thermal printing is performed, the recording medium is exposed to air at 40° C. and 90% relative humidity for 24 hours, then removed and cooled.
16 . The medium of claim 15 , wherein the print quality of the printed recording medium is still characterized by an ANSI value of at least 1.5 after the printed recording medium is exposed to air at 40° C. and 90% relative humidity for 24 hours, then removed and cooled.
17 . The medium of claim 1 , wherein the at least one developer comprises TGMD and a print quality of the recording medium when printed with a thermal printer energy setting of 11.7 mJ/mm 2 at a print speed of 6 inches per second (ips) is characterized by an ANSI value of at least 1.5.
18 . The medium of claim 17 , wherein the print quality of the printed recording medium is characterized by an ANSI value of at least 1.5 even where, before the thermal printing is performed, the recording medium is exposed to air at 40° C. and 90% relative humidity for 24 hours, then removed and cooled.
19 . The medium of claim 18 , wherein the print quality of the printed recording medium is still characterized by an ANSI value of at least 1.5 after the printed recording medium is exposed to air at 40° C. and 90% relative humidity for 24 hours, then removed and cooled.