MAGNETIZABLE CONCRETE COMPOSITION
A fresh concrete composition for producing a magnetizable concrete, including 250-450 kg/m 3 of cement, 50-150 kg/m 3 of a mineral addition, 2900-3500 kg/m 3 of aggregates containing magnetizable particles, and 100-150 kg/m 3 water, wherein the sand volume is ≥60 vol.-%.
1 . A fresh concrete composition for producing a magnetizable concrete, comprising:
cement,
at least one mineral addition,
aggregates, containing magnetizable particles, and
water,
wherein the aggregates volume is ≥60 vol.-%.
2 . The fresh concrete composition according to claim 1 , wherein the concrete composition comprises:
250-450 kg/m 3 of cement,
50-150 kg/m 3 of at least one mineral addition,
2900-3500 kg/m 3 of aggregates, containing magnetizable particles, and
100-200 kg/m 3 water.
3 . The fresh concrete composition according to claim 1 , wherein the aggregates are sand that comprises at least 60 wt.-%, of magnetizable material.
4 . The fresh concrete composition according to claim 1 , wherein the aggregates are sand having a volume that is 60-70 vol.-%.
5 . The fresh concrete composition according to claim 1 , wherein the concrete composition has a water/cement ratio W/C of ≤0.50.
6 . The fresh concrete composition according to claim 1 any one of claims 1 to 5 , wherein the magnetizable particles consist of ferrite.
7 . The fresh concrete composition according to claim 1 , wherein the mineral addition comprises or consists of silica fume, metakaolin, slag, pozzolans or mixtures thereof.
8 . The fresh concrete composition according to claim 1 , wherein the cement has a BET specific surface area of 1.20 to 5 m 2 /g.
9 . The fresh concrete composition according to claim 1 , wherein the mineral addition has a particle size distribution characterized by a D50 of ≤6 μm.
10 . The fresh concrete composition according to claim 1 , wherein the aggregates are sand that has a particle size distribution characterized by a D50≥50 μm and a D90≤4 mm.
11 . The fresh concrete composition according to claim 1 , wherein the concrete composition is free of aggregates having a particle size of >10 mm.
12 . The fresh concrete composition according to claim 1 , wherein the aggregates are sand that comprises a fine sand containing magnetizable particles and a coarse sand containing magnetizable particles, wherein the fine sand has a particle size distribution characterized by a D10 to a D90 of 0.063 to 1 mm and the coarse sand has a particle size distribution characterized by a D10 to a D90 of 1 to 5 mm.
13 . The fresh concrete composition according to claim 1 , wherein the concrete composition is substantially free of limestone.
14 . The fresh concrete composition according to claim 1 , wherein the magnetizable particles have a particle size distribution characterized by a D90 of 2-4 mm.
15 . The fresh concrete composition according to claim 1 , wherein the magnetizable particles have particle size distribution characterized by a D10 of 0.2-1 mm.
16 . A method of producing a magnetizable concrete, comprising preparing a fresh concrete composition according to claim 1 by mixing its constituents, casting the fresh concrete and allowing the fresh concrete to set and harden.
17 . A concrete made from a fresh concrete composition according to claim 1 .
18 . The concrete according to claim 17 , having a compressive strength after 28 days of >100 MPa.
19 . The concrete according to claim 17 , having an electromagnetic permeability of >40, measured according to the standard IEC 62044-2:2005.
20 . A concrete element made from a fresh concrete composition according to claims 1 , wherein the concrete element has a thickness of <170 mm.
21 . A method comprising providing a magnetizable concrete according to claim 17 for conducting an electromagnetic field emanating from an induction coil that is at least partly embedded in or supported by said concrete and is powered by an alternating current.