Porous poly(aryl ether ketone) membranes, processes for their preparation and use thereof
Porous poly(aryl ether ketone) (PAEK) articles are prepared from PAEK/polyimide blends by selective chemical decomposition and subsequent removal of the polyimide phase. Porous PAEK articles exhibit highly interconnected pore structure and a narrow pore size distribution. The porous PAEK articles of the present invention can be utilized as a porous media for a broad range of applications, including membranes for fluid separations, such as microfiltration, ultrafiltration, nanofiltration, and as a sorption media.
1. A process for the preparation of a porous poly(aryl ether ketone) article comprising the steps of:
a. forming a blend of poly(aryl ether ketone) polymer with a polyimide,
b. forming a shaped article from said blend by extrusion, casting or molding,
c. decomposing said polyimide in said shaped article into low molecular weight fragments by chemical means by contacting the shaped article with ammonia, tetraalkylammonium hydroxide, primary aliphatic amine, secondary aliphatic amine, or a mixture thereof,
d. removing said low molecular weight fragments from said article.
2. The process of claim 1 wherein said shaped article is subjected to annealing prior to step c).
3. The process of claim 1 wherein said steps c) and d) take place concurrently in a common liquid media.
4. The process of claim 1 further comprising drying the porous article under conditions that substantially preserves the porous structure.
5. The process of claim 4 wherein said drying process is carried out from a hydrocarbon or a fluorocarbon solvent.
6. The process of claim 5 wherein said hydrocarbon is pentane, hexane, cyclohexane, heptane, octane or a mixture thereof, and said flouorocarbon is a chlorofluorocarbon or a perfluorocarbon.
7. The process of claim 2 wherein said poly(aryl ether ketone) is poly(ether ether ketone) or poly(ether ketone).
8. The process of claim 7 wherein polyimide in said poly(aryl ether ketone)/polyimide blend is poly(ether imide) of the following repeat unit:
9. The process of claim 8 wherein said poly(ether imide) has a molecular weight between 1,000 and 500,000.
10. The process of claim 8 wherein said poly(ether ether ketone) or poly(ether ketone) comprises from 5 to 95 weight percent of said blend.
11. The process of claim 10 wherein said poly(ether ether ketone) or poly(ether ketone) comprises from 20 to 80 weight percent of said blend.
12. The process of claim 7 wherein polyimide in said poly(aryl ether ketone)/polyimide blend is the phenylindane containing polyimide of the following repeat unit:
13. The process of claim 12 wherein said phenylindane containing polyimide has a molecular weight between 1,000 and 500,000.
14. The process of claim 13 wherein said poly(ether ether ketone) or poly(ether ketone) comprises from 20 to 80 weight percent of said blend.
15. The process of claim 2 wherein said porous article is a flat sheet, a fiber, a tube, or a hollow fiber.
16. The process of claim 1 wherein said tetraalkyammonium hydroxide is tetramethylammonium hydroxide.
17. The process of claim 1 wherein said primary aliphatic amine is monoethanolamine, ethylamine, propylamine, butylamine, or a mixture thereof.
18. The process of claim 1 wherein said ammonia, tetraalkylammonium hydroxide, primary aliphatic amine, secondary aliphatic amine are in a solution of alcohol, hydrocarbon, ketone, water, aprotic solvent or a mixture thereof.
19. The process of claim 2 wherein said annealing step is carried out at a temperature between 200° C. and 300° C.
20. The process of claim 15 wherein said flat sheet, said fiber, said tube, or said hollow fiber is drawn prior to step c), after step d) or both.
21. The process of claim 15 wherein said flat sheet, said tube, or said hollow fiber is a fluid separation membrane.
22. The process of claim 15 wherein said article is a battery separator.
23. The process of claim 1 wherein said shaped poly(aryl ether ketone) article is a multilayer article formed from two or more poly(aryl ether ketone) polymer polyimide blends that differ in blend chemical composition.
24. The process of claim 23 wherein the poly(aryl ether ketone) polymer weight content in said blends differ by at least 1 percent.
25. The process of claim 23 wherein said shaped article is annealed prior to step c).
26. The process of claim 1 wherein said blend of poly(aryl ether ketone) with polyimide contains an additive.
27. The process of claim 26 wherein said additive is a solvent, a plasticizer, or a filler.
28. The process of claim 1 wherein the specific surface area of said article is above 20 m 2 /g.
29. The process of claim 28 wherein said polyimide is decomposed by contacting the shaped article with a primary aliphatic amine.
30. The process of claim 29 wherein said primary aliphatic amine is in a solution of alcohol, hydrocarbon, ketone, water, aprotic solvent or a mixture thereof.