Magnetic recording medium
The present invention provides a high recording density magnetic recording medium with excellent surface smoothness, as well as excellent electromagnetic conversion characteristics and durability. A magnetic recording medium comprising a lower non-magnetic layer containing at least a non-magnetic powder and a binder resin on a non-magnetic support, and an upper magnetic layer with a thickness of 0.2 μm or less on said lower non-magnetic layer, wherein said lower non-magnetic layer contains an acicular powder of hydrated iron oxide as the non-magnetic powder, and said lower non-magnetic layer contains a fatty acid and a fatty acid amide. Preferably the acicular powder of hydrated iron oxide is goethite with an average long axial length of 0.15 μm or less.
1. A magnetic recording medium comprising a lower non-magnetic layer containing at least a non-magnetic powder and a binder resin on a non-magnetic support, and an upper magnetic layer with a thickness of 0.2 μm or less on said lower non-magnetic layer, wherein said lower non-magnetic layer contains an acicular powder of hydrated iron oxide as the non-magnetic powder of a quantity in a range of approximately 40% to 80% by weight of the lower non-magnetic layer, and said lower non-magnetic layer contains a fatty acid and a fatty acid amide, a quantity of the fatty acid by weight being in an approximate range of 0.8 to 4.0 parts relative to 100 parts by weight of the acicular powder of hydrated iron oxide and a quantity of the fatty acid amide by weight being in an approximate range of 0.4 to 2.0 parts relative to 100 parts by weight of the acicular powder of hydrated iron oxide.
2. The magnetic recording medium according to claim 1 , wherein said acicular powder of hydrated iron oxide has an average long axial length of 0.15 μm or less.
3. The magnetic recording medium according to claim 1 , wherein said binder resin of said lower non-magnetic layer is a radiation curing binder resin.
4. The magnetic recording medium according to claim 1 , wherein the acicular powder of hydrated iron oxide is substantially acicular goethite.
5. The magnetic recording medium according to claim 4 , wherein the acicular goethite has an average long axial length of 0.20 μm or less.