Manufacturing method of heat exchanger and structure thereof
A first plate and a second plate have brazing paste on the surface thereof. When the first plate is combined with the second plate while an inner fin is disposed therein, a protrusion forms a clearance there between. Heat is added to evaporate the organic substances in the brazing paste. The organic substances vapor is discharged into outside of the tube through the clearance. After that, heat is added furthermore to melt the brazing paste. The first plate and the second plate are brazed together to form the tube and the inner fin is brazed to the inside of the tube.
1. A manufacturing method of a heat exchanger comprising:
an arranging step for combining a first plate with a second plate in such a manner that opening peripheries are confronting each other while an inner fin is disposed there between, the first plate and the second plate having a substantially U-shaped cross section, the first plate and the second plate being provided with a brazing material layer thereon;
an evaporating step in which the combined plates and the inner fin are heated so that the organic substances in the brazing material layer evaporate, and
a bonding step for bonding the first plate and the second plate together with the inner fin after the brazing material melts, wherein
a clearance is formed between the first plate and the second plate in the arranging step, and
an organic substances vapor is discharged from an inside of the first plate and the second plate through the clearance in the evaporating step.
2. The manufacturing method of an heat exchanger according to claim 1 , wherein
the first plate and the second plate are arranged in such a manner that the clearance has 0.05 mm to 0.2 mm of width in the arranging step.
3. The manufacturing method of an heat exchanger according to claim 1 , wherein
a spacer is disposed to form the clearance in the arranging step.
4. The manufacturing method of an heat exchanger according to claim 3 , wherein
the spacer is integrally provided on at least one of the first plate and the second plate.
5. The manufacturing method of an heat exchanger according to claim 1 , wherein
the first plate and the second plate are made of copper alloy containing zinc.
6. The manufacturing method of an heat exchanger according to claim 5 , wherein
the copper alloy contains 5 wt % or more of zinc.
7. The manufacturing method of heat exchanger according to claim 1 , wherein
an assembly of the first plate and the second plate is heated in gas including reduction gas or inactive gas in the evaporating step.
8. The manufacturing method of heat exchanger according to claim 7 , wherein
the gas including the reduction gas or the inactive gas flows between the first plate and the second plate in the evaporating step.
9. The manufacturing method of the heat exchanger according to claim 1 , wherein
the organic substances include a hydrocarbon.
10. A heat exchanger comprising:
a tube configured by combining a first plate with a second plate in such a manner that an outer periphery confronts to each other, the first plate and the second plate having substantially U-shaped cross section; and
an inner fin bonded in the tube by brazing paste, wherein
the tube has a spacer to form a clearance between the first plate and the second plate, the clearance existing until the first plate and the second plate are bonded.
11. The heat exchanger according to claim 10 , wherein
the spacer is integrally provided on at least one of the first plate and the second plate.
12. The heat exchanger according to claim 10 , wherein
the first plate and the second plate are made of copper alloy containing zinc.
13. The heat exchanger according to claim 12 , wherein the copper alloy contains 5 wt % or more of zinc.
14. The heat exchanger according to claim 10 , wherein the clearance has 0.05 mm to 0.2 mm of width.