Three-dimensional periodic structure and fabrication method thereof
A photonic crystal comprises a matrix constituting said three-dimensional periodic structure, a first lattice formed in said matrix by first spherical voids having a uniform first diameter, said first spherical voids forming a face-centered cubic lattice, and a second lattice formed in said matrix by second spherical voids having a uniform second diameter smaller than said first diameter, said second spherical voids occupying interstitial sites of said first spherical voids.
1. A photonic crystal, comprising:
a matrix constituting a three-dimensional periodic structure;
a first lattice formed in said matrix by first spherical voids having a uniform first diameter, said first spherical voids forming a face-centered cubic lattice; and
a second lattice formed in said matrix by second spherical voids having a uniform second diameter smaller than said first diameter, said second spherical voids occupying interstitial sites of said first spherical voids.
2. The photonic crystal as claimed in claim 1 , wherein said second lattice forms a face-centered cubic lattice.
3. The photonic crystal as claimed in claim 1 , wherein said matrix comprises titanium oxide.
4. The photonic crystal as claimed in claim 1 , wherein said second spherical voids have a diameter chosen so as to settle into said interstitial sites formed by said first spherical voids.
5. The photonic crystal as claimed in claim 1 , wherein said first spherical voids have a uniform diameter of about 300 nm, and wherein said second spherical voids have a uniform diameter of 32–34 nm.
6. The photonic crystal as claimed in claim 5 , wherein said second spherical voids have a diameter of about 33 nm.
7. An optical element including an optical waveguide, said optical waveguide including a cladding layer of a photonic crystal and an optical path formed in said photonic crystal, said photonic crystal comprising:
a matrix constituting a three-dimensional periodic structure;
a first lattice formed in said matrix by first spherical voids having a uniform first diameter, said first spherical voids forming a face-centered cubic lattice; and
a second lattice formed in said matrix by second spherical voids having a uniform second diameter smaller than said first diameter, said second spherical voids occupying interstitial sites of said first spherical voids.
8. The photonic crystal as claimed in claim 7 , wherein said second lattice forms a face-centered cubic lattice.
9. The photonic crystal as claimed in claim 7 , wherein said matrix comprises titanium oxide.
10. The photonic crystal as claimed in claim 7 , wherein said second spherical voids have a diameter chosen so as to settle into said interstitial sites formed by said first spherical voids.
11. The photonic crystal as claimed in claim 7 , wherein said first spherical voids have a uniform diameter of about 300 nm, and wherein said second spherical voids have a uniform diameter of 32–34 nm.
12. The photonic crystal as claimed in claim 11 , wherein said second spherical voids have a diameter of about 33 nm.
13. A three-dimensional periodic structure comprising:
a first lattice of first particles having a uniform first diameter, said first particles forming a face-centered cubic lattice; and
a second lattice of second particles having a uniform second diameter smaller than said first diameter, said second particles occupying interstitial sites of said first particles,
wherein remaining interstitial sites in the three-dimensional periodic structure are filled with a third material.
14. The three-dimensional periodic structure as claimed in claim 13 , wherein said second lattice forms a face-centered cubic lattice.
15. A three-dimensional periodic structure, comprising:
a matrix constituting said three-dimensional periodic structure;
a first lattice formed in said matrix by spherical voids having a uniform first diameter, said spherical voids forming a face-centered cubic lattice; and
a second lattice formed in said matrix by spherical particles having a uniform second diameter smaller than said first diameter, said second spherical particles occupying interstitial sites of said first spherical voids.
16. A three-dimensional periodic structure, comprising:
a matrix constituting said three-dimensional periodic structure;
a first lattice formed in said matrix by first spherical voids having a uniform first diameter, said first spherical voids forming a face-centered cubic lattice; and
a second lattice formed in said matrix by second spherical voids having a uniform second diameter smaller than said first diameter, said second spherical voids occupying interstitial sites of said first spherical voids.
17. The three-dimensional periodic structure as claimed in claim 16 , wherein said second lattice forms a face-centered cubic lattice.
18. A method of forming a three-dimensional periodic structure, comprising the steps of:
supplying a first suspension of generally spherical first particles having a first diameter into a gap formed by a pair of substrates to form an ordered structure of said first particles in said gap;
supplying a second suspension of generally spherical second particles having a second smaller diameter into said gap such that said second particles settle in interstitial sites of said first particles;
removing a dispersion medium of said first and second suspensions from said gap; and
filling remaining interstitial sites with a third material to form a matrix.
19. The method as claimed in claim 18 , wherein said second particles form a face-centered cubic lattice.
20. The method as claimed in claim 18 , wherein said step of supplying said second particles is conducted in a state in which there remains a film of a dispersion medium of said first suspension between adjacent first particles.
21. The method as claimed in claim 18 , wherein said second particles have a diameter so as to settle in said interstitial sites formed by said first particles.
22. The method as claimed in claim 21 , wherein said first particles have a uniform diameter of about 300 nm and said second particles have a uniform diameter of 32–34 nm.
23. The method as claimed in claim 22 , wherein said second particles have a uniform diameter of about 33 nm.
24. The method as claimed in claim 18 , further comprising the step of removing at least said first particles selectively with respect to said matrix.
25. The method as claimed in claim 24 , wherein said first and second particles comprise any of polystyrene and silica, and wherein said third material comprises titanium oxide.
26. The method as claimed in claim 24 , wherein said step of removing said first particles is conducted such that said second particles are removed simultaneously.