Process for making a flowable and meterable densified fiber particle
Discrete particles of cellulosic material are flowable and meterable. They are easily dispersible in an aqueous or a dry medium. The particles comprise singulated cellulose fibers that have been densified. The particles have a density of at least 0.3 g/cc.
1. A process for producing a readily dispersible, flowable, and meterable cellulosic product consisting essentially of:
singulating cellulose fibers derived from softwood by introducing never dried pulp fibers into a jet drier and drying and singulating the pulp fibers therein to form a mass consisting essentially of dried, singulated cellulose fibers and
densifying the mass of dried singulated fibers and forming the fibers into discrete particles, each of said discrete particles consisting essentially of a plurality of dried, singulated cellulose fibers and that are mechanically bonded together, said particles dispersing into singulated fibers in less than one minute with agitation.
2. The process of claim 1 , wherein said fibers are densified by passing the mass of singulated fibers through a pair of nip rolls to produce a mat of densified fibers.
3. The process of claim 2 , wherein said densified fibers are formed into discrete particles by cutting said mat of densified fibers into a plurality of discrete particles.
4. The process of claim 2 , wherein said fibers are formed into discrete particles by punching said mat of densified fibers to form discrete particles.
5. The process of claim 1 , wherein said fibers are simultaneously densified and formed by introducing said singulated cellulose fibers into a rotary die to form discrete particles.
6. The process of claim 1 , wherein said discrete particles have a density of at least 0.3 g/cc.
7. The process of claim 6 , wherein said density ranges from 0.3 to 2 g/cc.
8. The process of claim 6 , wherein said density ranges from 0.3 to 1 g/cc.
9. The process of claim 6 , wherein said particles are generally flat and have a total surface area of at least 10 sq. mm.
10. The process of claim 9 , wherein said particles have a surface area of about 10 to about 150 sq. mm.
11. The process of claim 1 , wherein said particles have a thickness of 0.5 mm or greater.
12. The process of claim 11 , wherein said thickness ranges from 0.5 to 10mm.
13. The process of claim 1 , wherein said cellulose fibers further comprise an adjuvant selected from the group consisting of coupling agents, silicates, zeolites, latices, crosslinkers, debonders, surfactants, dispersants, clays, carbonates, biocides, dyes, antimicrobial compositions, flame retardants, and preservatives.