Rubber prepared with precipitated silica and carbon black pellet composites of controlled hardness and tire with component derived therefrom
This invention relates to a rubber composition prepared with reinforcement comprised of a combination of precipitated silica aggregates and pelletized rubber reinforcing carbon black composites of carbon black and organic binder of a controlled hardness and to a tire with at least one component comprised of and derived from such rubber composition in which said carbon black pellet composites are disintegrated (fragmented) in situ within said rubber composition in the presence of particulate precipitated silica and silica coupling agent. In one aspect the invention relates to a tire having a component of a rubber composition comprised of at least one conjugated diene-based elastomer and reinforcing filler comprised of a combination of precipitated silica, silica coupling agent and fragmented rubber reinforcing carbon black pellet composites, said pellets having a controlled hardness value.
1. A tire having a tread of a rubber composition comprised of, based upon parts by weight per 100 parts by weight rubber (phr):
(A) at least one conjugated diene-based elastomer (100 phr);
(B) about 20 to about 120 phr of reinforcing filler comprised of:
(1) about 10 to about 110 phr of precipitated silica,
(2) about 10 to about 110 phr of carbon black pellets, and
(C) a coupling agent for said precipitated silica having a moiety reactive with hydroxyl groups contained on the surface of said precipitated silica and another different moiety interactive with said conjugated diene based elastomer(s);
wherein said carbon black pellets are composites comprised of rubber reinforcing carbon black and an organic binder;
wherein said carbon black pellets have a hardness value (ASTM D3313-88) in a range of from about 20 to about 35,
wherein said rubber reinforcing carbon black has an Iodine value (ASTM D1510) in a range of from about 20 to about 200 g/kg and a DBP (dibutyl phthalate) value (ASTM D2414) in a range of from about 50 to about 200 cc/100 g, and
wherein said conjugated diene-based elastomer is selected from polymers and copolymers of at least one of isoprene and 1,3-butadiene and copolymers of styrene and at least one of isoprene and 1,3-butadiene, and their mixtures.
2. The tire of claim 1 wherein said carbon black pellets are in a form of disintegrated fragments thereof.