Method for producing low-odor hydrogel-forming polymers
This invention relates to a process for preparing a low-odor hydrogel-forming acrylic acid polymer, which comprises the steps of: a) preparing a polymeric hydrogel by free-radically polymerizing a monomer composition comprising at least 50% by weight of acrylic acid in an aqueous polymerization medium and converting said hydrogel into a particulate hydrogel or into hydrogel-forming powder; and optionally b) treating said particulate hydrogel or said hydrogel-forming powder with a crosslinking substance which, actually or latently, contain at least two functional groups capable of reacting with the carboxyl groups on the addition polymer; characterized by the acrylic acid used in step a) containing less than 400 ppm of acetic acid and propionic acid. It further relates to the hydrogel-forming addition polymers obtainable by the process and to their use.
1. A process for preparing a low-odor hydrogel-forming acrylic acid polymer, which comprises the steps of:
a) preparing a polymeric hydrogel by free-radically polymerizing a monomer composition comprising at least 50% by weight of acrylic acid containing volatile saturated carboxylic acids selected from the group consisting of acetic acid, propionic acid and combinations thereof as impurities in a total amount of less than 400 ppm, by weight, based on the amount of acrylic acid, in an aqueous polymerization medium and converting said hydrogel into a particulate hydrogel or into hydrogel-forming powder; and
b) treating said particulate hydrogel or said hydrogel-forming powder with a crosslinking substance which, actually or latently, contains at least two functional groups capable of reacting with the carboxyl groups on the addition polymer.
2. The process as claimed in claim 1 , wherein the acrylic acid polymerized in step a) is an acrylic acid obtained by a single or multiple stage crystallization of a crude acrylic acid having an acetic and/or propionic acid content in the range from 0.1 to 5% by weight.
3. The process as claimed in claim 2 , wherein the acrylic acid monomer of step a) is obtained by single or multiple stage crystallization of said crude acrylic acid at a temperature ranging from 0 to 13° C.
4. The process as claimed in claim 1 , wherein the acrylic acid monomer of step a) is in the form of a partially or completely neutralized aqueous acrylic acid solution.
5. The process as claimed in claim 1 , wherein the crosslinker in step b) is selected from compounds capable of forming ester groups with the carboxyl groups on the addition polymer.
6. The process as claimed in claim 1 , wherein the monomer mixture to be polymerized in step a) comprises, based on its total weight,
from 50 to 99.99% by weight of acrylic acid as monomer A,
from 0 to 49.99% by weight of one or more monoethylenically unsaturated monomers B which are copolymerizable with acrylic acid, and
from 0.01 to 30% by weight of at least one crosslinking compound C.
7. The process as claimed in claim 1 , wherein the acrylic acid monomer contains not more than 300 ppm of acetic acid, propionic acid or combinations thereof.
8. The process as claimed in claim 1 , wherein the acrylic acid monomer contains not more than 200 ppm of acetic acid, propionic acid or combinations thereof.
9. A hydrogel-forming addition polymer obtainable by a process as claimed in claim 1 .
10. A method for preparing a hygiene article comprising:
forming the hydrogel-forming addition polymer as claimed in claim 9 into a shape of said hygiene article.
11. Hygiene articles comprising an absorbent core which contains at least one hydrogel-forming addition polymer as claimed in claim 9 .