Adhesive with multistage curing and the utilization thereof during the production of composite materials
The invention relates to an adhesive containing two components A and B, whereby component A comprises both a functional group which can be polymerized by means of irradiation with UV beams as well as at least one functional group which is able to react with a compound having at least one acidic hydrogen atom and component B comprises at least two functional groups which can be polymerized by means of irradiation with UV beams or with electron beams. The adhesive is suitable for the production of composite materials and exhibits a high flexibility with a good initial bonding.
1. A flexible laminate comprising:
a first substrate consisting of plastic film;
a second substrate selected from the group consisting of plastic film and metal foil; and
an irradiated adhesive composition positioned between the first and second substrate, the adhesive composition comprising components A, B and D,
(a) component A being at least one polymer having a molecular weight (M n ) of at least 800 that has at least one functional group polymerizable by irradiation with ultraviolet (UV) light or with electron beams and has at least one functional group selected from the group consisting of isocyanate groups and epoxy groups; capable of reacting with a compound having at least one acidic hydrogen atom,
(b) component B being at least one compound having a molecular weight (M n ) of from about 100 to about 8000 which has at least two functional groups polymerizable by irradiation with UV light or with electron beams; and
(c) component D being a compound having at least two acidic hydrogen atoms, wherein component A, component B and component D are each a different compound.
2. The flexible laminate of claim 1 wherein in the adhesive composition the at least one functional group polymerizable by irradiation with UV light or with electron beams of component A comprises a group having an olefinically unsaturated double bond.
3. The flexible laminate of claim 2 wherein in the adhesive composition component B comprises at least two groups having an olefinically unsaturated double bond as functional groups polymerizable by irradiation with UV light or with electron beams.
4. The flexible laminate of claim 1 wherein in the adhesive composition component B comprises at least two groups having an olefinically unsaturated double bond as the functional groups polymerizable by irradiation with UV light or with electron beams.
5. The flexible laminate of claim 1 wherein in the adhesive composition component A is a polymer selected from the group consisting of polyacrylates, polyesters, polyethers, polycarbonates, polyacetals, polyurethanes, polyolefins, nitrile rubber, styrene/butadiene rubber, and combinations thereof.
6. The flexible laminate of claim 1 wherein in the adhesive composition component A comprises at least one polyurethane.
7. The flexible laminate of claim 1 wherein the adhesive composition possesses a viscosity at 70 □C of from 1000 mPas to 6000 mPas.
8. The flexible laminate of claim 1 which further comprises
(c) as component C at least one photoinitiator which is capable of initiating the polymerization of olefinically unsaturated double bonds on exposure to UV radiation.
9. The flexible laminate of claim 8 wherein component C comprises at least one photoinitiator obtained by reacting a polyfunctional alcohol having two or more OH groups with a di- or triisocyanate and a photoinitiator having at least two isocyanate-reactive functional groups and which is capable of initiating the polymerization of olefinically unsaturated double bonds on exposure to UV radiation.
10. The flexible laminate of claim 9 wherein component C comprises a photoinitiator obtained by reacting an at least trihydric alcohol with caprolactone to give a polycaprolactone which carries at least three OH groups and has a molecular weight of from about 300 to about 900, and subsequently linking the polycaprolactone with 1-[4-(2-hydroxyethoxy) phenyl]-2-hydroxy-2-methylpropan-1-one by means of a compound which carries at least two isocyanate groups.
11. The flexible laminate of claim 1 wherein a compound having at least two OH groups is present as component D.
12. The flexible laminate of claim 1 wherein in the adhesive composition component B is an ester of acrylic acid or methacrylic acid with a polyol selected from the group consisting of aromatic polyols, aliphatic polyols and cycloaliphatic polyols, or an acrylate ester of polyether alcohols.
13. A method for producing flexible composite materials, the method comprising:
applying an adhesive composition to at least a portion of a first substrate, said first substrate consisting of a plastic film, the adhesive composition comprising components A, B and D:
(a) component A being at least one polymer having a molecular weight (M n ) of at least 800 that has at least one functional group polymerizable by irradiation with UV light or with electron beams and has at least one functional group “selected from the group consisting of isocyanate groups and epoxy groups”; capable of reacting with a compound having at least one acidic hydrogen atom;
(b) component B being at least one compound having a molecular weight (M n ) of from about 100 to about 8000 which has at least two functional groups polymerizable by irradiation with UV light or with electron beams; and
(c) component D being a compound having at least two acidic hydrogen atoms, wherein component A, component B and component D are each different compounds;
irradiating the applied adhesive with UV light or electron beams; and, contacting the irradiated adhesive with a second substrate consisting of metal foil.
14. The method of claim 13 wherein in the adhesive composition the at least one functional group polymerizable by irradiation with UV light or with electron beams of component A comprises a group having an olefinically unsaturated double bond.
15. The method of claim 14 wherein in the adhesive composition component B comprises at least two groups having an olefinically unsaturated double bond as functional groups polymerizable by irradiation with UV light or with electron beams.
16. The method of claim 13 wherein in the adhesive composition component A comprises an isocyanate group as the functional group capable of reacting with a compound having at least one acidic hydrogen atom.
17. The method of claim 13 wherein in the adhesive composition component A comprises a group having an olefinically unsaturated bond as the at least one functional group polymerizable by irradiation with UV light or with electron beams and an isocyanate group as the at least one functional group capable of reacting with a compound having at least one acidic hydrogen atom.
18. The method of claim 13 wherein in the adhesive composition component B comprises at least two groups having an olefinically unsaturated double bond as the functional groups polymerizable by irradiation with UV light or with electron beams.
19. The method of claim 13 wherein in the adhesive composition component A is a polymer selected from the group consisting of polyacrylates, polyesters, polyethers, polycarbonates, polyacetals, polyurethanes, polyolefins, nitrile rubber, styrene/butadiene rubber, and combinations thereof.
20. The method of claim 13 wherein the adhesive composition further comprises
(c) as component C at least one photoinitiator which is capable of initiating the polymerization of olefinically unsaturated double bonds on exposure to UV radiation.
21. The method of claim 20 wherein component C comprises at least one photoinitiator obtained by reacting a polyfunctional alcohol having two or more OH groups with a di- or triisocyanate and a photoinitiator having at least two isocyanate-reactive functional groups and which is capable of initiating the polymerization of olefinically unsaturated double bonds on exposure to UV radiation.
22. The method of claim 21 wherein component C comprises a photoinitiator obtained by reacting an at least trihydric alcohol with caprolactone to give a polycaprolactone which carries at least three OH groups and has a molecular weight of from about 300 to about 900, and subsequently linking the polycaprolactone with 1-[4-(2-hydroxyethoxy) phenyl]-2-hydroxy-2-methylpropan-1-one by means of a compound which carries at least two isocyanate groups.
23. The method of claim 13 wherein a compound having at least two OH groups is present as component D.
24. The method of claim 13 wherein in the adhesive composition component B is an ester of acrylic acid or methacrylic acid with a polyol selected from the group consisting of aromatic polyols, aliphatic polyols and cycloaliphatic polyols, or an acrylate ester of polyether alcohols.
25. A flexible composite material comprising:
an irradiated adhesive composition sandwiched between a first substrate consisting of plastic film and a second substrate consisting of metal foil, the adhesive composition comprising
(a) component A being at least one polymer having a molecular weight (M n ) of at least 800 that has at least one functional group polymerizable by irradiation with UV light or with electron beams and has at least one functional group “selected from the group consisting of isocyanate groups and epoxy groups”, capable of reacting with a compound having at least one acidic hydrogen atom;
(b) component B being at least one compound having a molecular weight (M n ) of from about 100 to about 8000 which has at least two functional groups polymerizable by irradiation with UV light or with electron beams;
(c) component C being at least one photoinitiator having a molecular weight of more than about 200 and which is capable of initiating the polymerization of olefinically unsaturated double bonds on exposure to UV radiation; and,
(d) component D being a compound having at least two acidic hydrogen atoms, wherein component A, component B and component C and component D are each a different compound.
26. The flexible composite of claim 25 wherein in the irradiated adhesive composition component B is an ester of acrylic acid or methacrylic acid with a polyol selected from the group consisting of aromatic polyols, aliphatic polyols and cycloaliphatic polyols, or an acrylate ester of polyether alcohols.