Repair and reclassification of superalloy components
Novel materials and methods for repairing/reclassifying superalloy components are described herein. These materials are non-traditional blends of materials having a much higher base material content than traditional repair/reclassification materials. In embodiments used to repair/reclassify nickel-based components, these materials may comprise about 5-18.9 weight percent of a low melting point alloy and about 81.1-95 weight percent of a base material. In embodiments used to repair/reclassify cobalt-based components, these materials may comprise about 15-30 weight percent of a low melting point alloy and about 70-85 weight percent of a base material. These materials can be used to repair surface defects and/or build up worn or eroded areas of a component to meet precise dimensional and metallurgical requirements. These materials create robust repaired components having a dense, isothermally solidified structure having minimal borides and a high re-melt temperature.
1. A method of repairing surface defects and replacing material on a nickel-based metallic article, comprising:
depositing a first material on a predetermined area of the metallic article, the composition of the first material comprising about 30-50 weight percent low melting point alloy mixed with about 50-70 weight percent base material;
depositing a second material over the first material, the composition of the second material comprising about 5-18.9 weight percent low melting point alloy mixed with about 81.1-95 weight percent base material; and
heat treating the article at a predetermined temperature for a predetermined amount of time.
2. The method of claim 1 , wherein the predetermined temperature is about 1093-1260° C. and the predetermined time is about 4-20 hours.
3. The method of claim 1 , wherein the first material and the second material are deposited as a single graded layer, wherein the composition of the graded layer is similar to die composition of the first material as deposition initially begins, and then the composition of the graded layer varies to become similar to the composition of the second material as the graded layer continues to be deposited.
4. A method of repairing surface defects and replacing material on a cobalt-based metallic article, comprising:
depositing a first material on a predetermined area of the metallic article, the composition of the first material comprising about 40-50 weight percent low melting point alloy mixed with about 50-60 weight percent base material;
depositing a second material over the first material, the composition of the second material comprising about 15-30 weight percent low melting point alloy mixed with about 70-85 weight percent base material; and
heat treating the article at a predetermined temperature for a predetermined amount of time.
5. The method of claim 4 , wherein the predetermined temperature is about 1093-1260° C. and the predetermined time is about 4-20 hours.
6. The method of claim 4 , wherein the first material and the second material are deposited as a single graded layer, wherein the composition of the graded layer is similar to the composition of the first material as deposition initially begins, and then the composition of the graded layer varies to become similar to the composition of the second material as the graded layer continues to be deposited.