Terpolymer compositions for coating substrates used in computer printers
Terpolymer compositions of vinyl caprolactam (VCL), dimethylaminopropyl methacrylamide (DMAPMA) and hydroxyethyl methacrylate (HEMA) are described to coat substrates for use in computer printers, and provide advantageous print quality thereon.
1. A formulation including a terpolymer composition consisting essentially of vinyl caprolactam (VCL), dimethylaminopropyl methacrylamide (DMAPMA) and hydroxyethyl methacrylate (HEMA), uncrosslinked or crosslinked, unquaternized or quaternized, which exhibits light stability to dyes found in ink-jet printers, as evidenced by a less than 25% color fading in the ASTM G-53-84 test.
2. A formulation according to claim 1 which includes another water soluble ingredient.
3. A formulation according to claim 2 wherein said ingredient is polyvinylalcohol (PVA), polyvinylpyrrolidone, acrylate, styrene-butadiene latex, gelatin, poly(2-ethyl-2-oxazoline), and/or a cellulosic polymer.
4. A formulation according to claim 2 wherein said ingredient is an inorganic pigment selected from a silicate, aluminate, zirconate, barium sulfate, calcium carbonate and clay.
5. A formulation according to claim 1 wherein the terpolymer is uncrosslinked.
6. A formulation according to claim 1 wherein the terpolymer is crosslinked.
7. A formulation according to claim 1 wherein the terpolymer is unquaternized.
8. A formulation according to claim 1 wherein the terpolymer is quaternized.
9. A formulation according to claim 1 wherein the terpolymer is crosslinked and quaternized.
10. A formulation according to claim 1 wherein the terpolymer composition comprises by wt., 60-90% VCL, 10-30% DMAPMA and 2-10% HEMA.
11. A formulation according to claim 10 wherein the terpolymer composition comprises by wt., 75-80% VCL, 13-16% DMAPMA and 4-6% HEMA.
12. A formulation according to claim 10 wherein the terpolymer composition includes up to about 0.8% of a crosslinking agent.
13. A formulation according to claim 10 wherein the terpolymer composition comprises up to 40% of a quaternizing agent.
14. A formulation according to claim 10 wherein the terpolymer composition comprises a crosslinking agent and the crosslinking agent is pentaerythriol triallyl ether (PETE).
15. A formulation according to claim 10 wherein the terpolymer composition comprises a crosslinking agent present in an amount of 0.5-0.7% by wt. of the terpolymer.