Room temperature-curable organopolysiloxane compositions

1. A room temperature-curable organopolysiloxane composition comprising

(A) 100 parts by weight of a diorganopolysiloxane having hydroxyl groups at both ends and/or a diorganopolysiloxane having alkoxysilyl groups at both ends,

(B) 0.1 to 10 parts by weight of a polyoxypropylene-modified silicone having the general formula (1), (2) or (3):

wherein R is each independently a substituted or unsubstituted monovalent hydrocarbon group, Y is —R 1 —O—(C 3 H 6 O) j —H, R 1 is an alkylene group of 1 to 12 carbon atoms, k is an integer of at least 1, m is an integer of at least 1, k+m is an integer of at least 10, n is an integer of at least 4, and j is an integer of at least 5,

(C) 1 to 50 parts by weight of wet silica having a water content of up to 1% by weight and prepared by using sodium silicate derived from silica sand as raw material, neutralizing an aqueous solution of sodium silicate, allowing silica to precipitate, followed by filtration and drying, or subjecting an alkoxysilane to hydrolysis reaction,

said wet silica having a BET specific surface area of greater than or equal to 50 square meters per gram (m 2 /g), and

(D) 1 to 20 parts by weight of a silane or siloxane having at least three hydrolyzable groups bonded to silicon atoms in a molecule.

2. The composition of claim 1 , further comprising (B) 0.01 to 10 parts by weight of a cure catalyst.

3. The composition of claim 1 , further comprising (F) 0.1 to 20 parts by weight of a silane coupling agent.

4. The composition of claim 1 which is used as a sealing agent or adhesive.

5. The composition of claim 1 , wherein component A) is a diorganopolysiloxanes having the general formulae (4) or (5):

wherein

R 2 , which may be the same or different, is a substituted or unsubstituted monovalent hydrocarbon group of 1 to 10 carbon atoms,

R 3 , which may be the same or different, is a substituted or unsubstituted monovalent hydrocarbon group of 1 to 6 carbon atoms,

X is an oxygen atom or a substituted or unsubstituted divalent hydrocarbon group of 2 to 6 carbon atoms,

a is an integer of at least 10, and

n is an integer of 1 to 3.

6. The composition of claim 1 , wherein component A) has a viscosity of 100 to 1,000,000 mPa·s at 20° C.

7. The composition of claim 1 , wherein component C) has a ratio of BET specific surface area to CTAB specific surface area of from 1.0 to 1.3.

8. The composition of claim 1 , wherein the hydrolyzable group of component D) is selected from the group consisting of ketoxime, alkoxy, acetoxy, isopropenoxy and combinations thereof.

9. The composition of claim 1 , wherein component D) is a ketoxime silane, an alkoxysilane, an acetoxysilane, an isopropenoxysilane, a partial hydrolytic condensates of a ketoxime silane, partial hydrolytic condensates of an alkoxysilane, partial hydrolytic condensates of an acetoxysilane, partial hydrolytic condensates of an isopropenoxysilane or mixtures thereof.

10. The composition of claim 1 , comprising a solvent in an amount so that the composition is thixotropic.